- Chang Chun Plastic PBT2000 Fire Retardant PBT
Chang Chun Plastic PBT2000 Fire Retardant PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant |
| Manufacturer | Chang Chun Plastic Co. Ltd. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chang Chun Plastic PBT2000 Fire Retardant PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Dowell Trading Company Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 - 1.41 g/cc | 0.0502 - 0.0509 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.013 - 0.020 cm/cm | 0.013 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 88 | 88 | ASTM D785 |
| Tensile Strength, Ultimate | 50.0 - 70.0 MPa | 7250 - 10200 psi | ASTM D638 |
| Elongation at Break | 7.0 - 9.0 % | 7.0 - 9.0 % | ASTM D638 |
| Flexural Yield Strength | 70.0 - 80.0 MPa | 10200 - 11600 psi | ASTM D790 |
| Flexural Modulus | 2.00 - 3.00 GPa | 290 - 435 ksi | ASTM D790 |
| Izod Impact, Notched | 0.250 - 0.340 J/cm @Thickness 6.35 mm |
0.468 - 0.637 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C @Temperature 20.0 °C |
50.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Melting Point | 225 °C | 437 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | 1/32 in. |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 60 Hz |
3.2 @Frequency 60 Hz |
ASTM D150 |
| Dielectric Strength | 20.0 kV/mm @Thickness 2.00 mm |
508 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 60 Hz |
0.0010 @Frequency 60 Hz |
ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering F80R Fluorosilicone Rubber
- SABIC Innovative Plastics Lexan® OQ4320 PC (Europe-Africa-Middle East)
- Honeywell Capran® Oxyshield™ OEB (1.0 mil) Monoaxially Oriented, Co-Extruded Nylon6/EVOH/Nylon 6 Clear Film
- Michelman® Michem® Emulsion 52137 Nonionic polyethylene emulsion
- Solvay Specialty Polymers Torlon® 4630 Polyamide-imide (PAI)
- UBE UBEPOL BR150L Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 35 Minutes at 145°C)
- A. Schulman PP 3487-01 Polypropylene Homopolymer Polypropylene
- Borealis Bormed™ RD808CF Polypropylene Random Copolymer
- Dow Corning 9601 TEXTILE PRINTING INK
- EMS-Grivory Grivory® HT1V-4 FWA nat PA6T/6I-GF40
Copyright © lookpolymers.com All Rights Reserved