Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded
Manufacturer DSM Engineering Plastics
Trade Name Arnite®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Arnite® T06 202 /A PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medium Viscosity, Injection Molding
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
ISO 1183
Water Absorption 0.45 %
0.45 %
Sim. To ISO 62
Moisture Absorption 0.180 %
0.180 %
Sim. To ISO 62
Viscosity 12500 cP

@Shear Rate 100000 1/s,
Temperature 270 °C
 12500 cP

@Shear Rate 100000 1/s,
Temperature 518 °F
15000 cP

@Shear Rate 100000 1/s,
Temperature 230 °C
 15000 cP

@Shear Rate 100000 1/s,
Temperature 446 °F
15000 cP

@Shear Rate 100000 1/s,
Temperature 250 °C
 15000 cP

@Shear Rate 100000 1/s,
Temperature 482 °F
300000 cP

@Shear Rate 1.00 1/s,
Temperature 270 °C
 300000 cP

@Shear Rate 1.00 1/s,
Temperature 518 °F
500000 cP

@Shear Rate 1.00 1/s,
Temperature 250 °C
 500000 cP

@Shear Rate 1.00 1/s,
Temperature 482 °F
800000 cP

@Shear Rate 1.00 1/s,
Temperature 230 °C
 800000 cP

@Shear Rate 1.00 1/s,
Temperature 446 °F
Linear Mold Shrinkage, Flow 0.020 cm/cm
0.020 in/in
Sim. To ISO 294-4
Linear Mold Shrinkage, Transverse 0.020 cm/cm
0.020 in/in
Sim. To ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.0 MPa
7980 psi
ISO 527-1/-2
Elongation at Break 20 %
20 %
ISO 527-1/-2
Elongation at Yield 3.5 %
3.5 %
ISO 527-1/-2
Tensile Modulus 2.70 GPa
392 ksi
ISO 527-1/-2
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179/1eU
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
0.500 J/cm²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C
50.0 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C
50.0 µin/in-°F
ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi) 165 °C
329 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 IEC 60695-11-10
HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
 IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
 3.2

@Frequency 1.00e+6 Hz
 IEC 60250
3.5

@Frequency 100 Hz
 3.5

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 27.0 kV/mm
686 kV/in
IEC 60243-1
Dissipation Factor 0.0020

@Frequency 100 Hz
 0.0020

@Frequency 100 Hz
 IEC 60250
0.020

@Frequency 1.00e+6 Hz
 0.020

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112