DuPont Performance Polymers Delrin® FG500TL NC010 Acetal Homopolymer (Unverified Data**)

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, PTFE-Filled
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Delrin® FG500TL NC010 Acetal Homopolymer (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Delrin® FG500TL medium viscosity acetal homopolymer resin containing 1.5% Teflon® PTFE Micropowder. It has been developed for consideration into applications such as parts for the food industry.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.43 g/cc	0.0517 lb/in³	ISO 1183
Water Absorption	0.17 % @Temperature 23.0 °C	0.17 % @Temperature 73.4 °F	Equilibrium 50%RH; ISO 62, Similar to
	0.33 % @Temperature 23.0 °C	0.33 % @Temperature 73.4 °F	Immersion 24h; ISO 62, Similar to
	0.90 % @Temperature 23.0 °C	0.90 % @Temperature 73.4 °F	Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage, Flow	0.018 cm/cm @Thickness 2.00 mm	0.018 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.017 cm/cm @Thickness 2.00 mm	0.017 in/in @Thickness 0.0787 in	ISO 294-4
Melt Flow	14 g/10 min @Load 2.16 kg, Temperature 190 °C	14 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Melt Index of Compound	12 g/10 min @Load 2.16 kg, Temperature 190 °C	12 g/10 min @Load 4.76 lb, Temperature 374 °F	cm3/10 min; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	71.0 MPa @Temperature 23.0 °C	10300 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	20 % @Temperature 23.0 °C	20 % @Temperature 73.4 °F	nominal; ISO 527
Elongation at Yield	13 % @Temperature 23.0 °C	13 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	3.30 GPa @Temperature 23.0 °C	479 ksi @Temperature 73.4 °F	ISO 527
Flexural Modulus	3.10 GPa @Temperature 23.0 °C	450 ksi @Temperature 73.4 °F	ISO 178
Charpy Impact Unnotched	16.0 J/cm² @Temperature -30.0 °C	76.1 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
	17.0 J/cm² @Temperature 23.0 °C	80.9 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.400 J/cm² @Temperature -30.0 °C	1.90 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	0.500 J/cm² @Temperature 23.0 °C	2.38 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	500 µm/m-°C @Temperature -40.0 - 23.0 °C	278 µin/in-°F @Temperature -40.0 - 73.4 °F	ISO 11359-1/-2
	500 µm/m-°C @Temperature 23.0 - 55.0 °C	278 µin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1/-2
	500 µm/m-°C @Temperature 55.0 - 100 °C	278 µin/in-°F @Temperature 131 - 212 °F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	90.0 µm/m-°C @Temperature -40.0 - 23.0 °C	50.0 µin/in-°F @Temperature -40.0 - 73.4 °F	ISO 11359-1/-2
	100 µm/m-°C @Temperature 23.0 - 55.0 °C	55.6 µin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1/-2
	150 µm/m-°C @Temperature 55.0 - 100 °C	83.3 µin/in-°F @Temperature 131 - 212 °F	ISO 11359-1/-2
Melting Point	178 °C	352 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	165 °C	329 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	103 °C	217 °F	ISO 75-1/-2

Processing Properties	Metric	English	Comments
Melt Temperature	215 °C	419 °F	Optimum; Injection Molding
	210 - 220 °C	410 - 428 °F	Injection Molding
Mold Temperature	90.0 °C	194 °F	optimum; Injection Molding
	80.0 - 100 °C	176 - 212 °F	Injection Molding
Drying Temperature	80.0 °C	176 °F	Injection Molding
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour	Injection Molding
Moisture Content	<= 0.20 %	<= 0.20 %	Injection Molding

Descriptive Properties	Value	Comments
Appearance	Natural Color
Features	Creep Resistance, Good
	Fatigue Resistant
	Friction, Low
	Homopolymer
	Stiffness, High
	Strength, High
	Viscosity, Medium
	Wear Resistance, Good
Forms	Pellets
Generic	Acetal (POM) Homopolymer
Material Status	Preliminary Data
Part Marking Code	>POM-SD<	ISO 11469
Processing Method	Injection Molding
Product Category	Food Contact Resins
	Low Wear and Friction Resins
	Unreinforced Resins
Region Available - Global	Yes
Resin Identification	POM-SD	ISO 1043
RoHS Compliance	Contact Manufacturer
Uses	Food Applications, Non-specific
	Parts, Engineering