BASF Ultramid® 8202C PA6 (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® 8202C PA6 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique crystalline structure results in increased strength, stiffness, heat distortion temperature and performance under load as a homopolymer. It also cycles faster while maintaining properties and resistance.

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	ISO 1183
Water Absorption	1.6 %	1.6 %	24 hour; ISO Test
	9.3 %	9.3 %	ISO 62
Moisture Absorption at Equilibrium	2.6 %	2.6 %	23°C/50% R.H.; ISO 62
Relative Viscosity	2.6 cP	2.6 cP	ISO Test; 96 % SAV
Viscosity Measurement	48	48	Formic Acid
Linear Mold Shrinkage	0.0090 cm/cm	0.0090 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	ASTM Test
Tensile Strength at Break	90.0 MPa	13100 psi	0.2 in/min; ASTM Test
	25.0 MPa @Temperature 120 °C	3630 psi @Temperature 248 °F	ASTM Test
	25.0 MPa @Temperature 120 °C	3630 psi @Temperature 248 °F	ISO Data
	35.0 MPa @Temperature 80.0 °C	5080 psi @Temperature 176 °F	ISO Data
	35.0 MPa @Temperature 80.0 °C	5080 psi @Temperature 176 °F	ASTM Test
	130 MPa @Temperature -40.0 °C	18900 psi @Temperature -40.0 °F	ASTM Test
	130 MPa @Temperature -40.0 °C	18900 psi @Temperature -40.0 °F	ISO Data
Tensile Strength, Yield	88.0 MPa	12800 psi	50mm/min; ISO 527
	90.0 MPa	13100 psi	2 in/min; ASTM Test
	30.0 MPa @Temperature 120 °C	4350 psi @Temperature 248 °F	ASTM Test
	30.0 MPa @Temperature 120 °C	4350 psi @Temperature 248 °F	ISO Data
	40.0 MPa @Temperature 80.0 °C	5800 psi @Temperature 176 °F	ISO Data
	40.0 MPa @Temperature 80.0 °C	5800 psi @Temperature 176 °F	ASTM Test
	137 MPa @Temperature -40.0 °C	19900 psi @Temperature -40.0 °F	ASTM Test
	137 MPa @Temperature -40.0 °C	19900 psi @Temperature -40.0 °F	ISO Data
Elongation at Break	7.0 %	7.0 %	50mm/min, Nominal strain; ISO 527
	12 %	12 %	2 in/min; ASTM Test
	>= 100 %	>= 100 %
	5.0 % @Temperature -40.0 °C	5.0 % @Temperature -40.0 °F	ASTM Test
	5.0 % @Temperature -40.0 °C	5.0 % @Temperature -40.0 °F	ISO Data
	>= 100 % @Temperature 120 °C	>= 100 % @Temperature 248 °F	ISO Data
	>= 100 % @Temperature 80.0 °C	>= 100 % @Temperature 176 °F	ISO Data
	>= 100 % @Temperature 120 °C	>= 100 % @Temperature 248 °F	ASTM Test
Elongation at Yield	4.0 %	4.0 %	50mm/min; ISO 527
	4.0 %	4.0 %	2 in/min; ASTM Test
	3.0 % @Temperature -40.0 °C	3.0 % @Temperature -40.0 °F	ASTM Test
	3.0 % @Temperature -40.0 °C	3.0 % @Temperature -40.0 °F	ISO Data
	25 % @Temperature 80.0 °C	25 % @Temperature 176 °F	ASTM Test
	25 % @Temperature 80.0 °C	25 % @Temperature 176 °F	ISO Data
	27 % @Temperature 120 °C	27 % @Temperature 248 °F	ASTM Test
	27 % @Temperature 120 °C	27 % @Temperature 248 °F	ISO Data
Tensile Modulus	3.70 GPa	537 ksi	1mm/min; ISO 527
	0.550 GPa @Temperature 120 °C	79.8 ksi @Temperature 248 °F	ISO Data
	0.750 GPa @Temperature 80.0 °C	109 ksi @Temperature 176 °F	ISO Data
	4.09 GPa @Temperature -40.0 °C	593 ksi @Temperature -40.0 °F	ISO Data
Flexural Strength	95.0 MPa	13800 psi	ISO Data
	110 MPa	16000 psi	ASTM Test
	21.0 MPa @Temperature 120 °C	3050 psi @Temperature 248 °F	ASTM Test
	30.0 MPa @Temperature 65.0 °C	4350 psi @Temperature 149 °F	ASTM Test
	183 MPa @Temperature -40.0 °C	26500 psi @Temperature -40.0 °F	ASTM Test
Flexural Modulus	2.80 GPa	406 ksi	ISO Data
	3.17 GPa	460 ksi	ASTM Test
	0.385 GPa @Temperature 120 °C	55.8 ksi @Temperature 248 °F	ASTM Test
	0.440 GPa @Temperature 93.0 °C	63.8 ksi @Temperature 199 °F	ASTM Test
	0.600 GPa @Temperature 65.0 °C	87.0 ksi @Temperature 149 °F	ASTM Test
Izod Impact, Notched	0.320 J/cm @Temperature -40.0 °C	0.599 ft-lb/in @Temperature -40.0 °F	ASTM Test
	0.480 J/cm @Thickness 3.17 mm	0.899 ft-lb/in @Thickness 0.125 in	ASTM Test
Charpy Impact Unnotched	NB	NB	ISO 179
Charpy Impact, Notched	0.350 J/cm²	1.67 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear	81.0 µm/m-°C @Temperature -30.0 - 30.0 °C	45.0 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM Test
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test
Deflection Temperature at 0.46 MPa (66 psi)	165 °C	329 °F	ISO 75
	190 °C	374 °F	ASTM Test
Deflection Temperature at 1.8 MPa (264 psi)	65.0 °C	149 °F	ISO 75
	75.0 °C	167 °F	ASTM Test
Flammability, UL94	V-2 @Thickness 0.700 mm	V-2 @Thickness 0.0276 in
	V-2 @Thickness 3.00 mm	V-2 @Thickness 0.118 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Comparative Tracking Index	600 V	600 V	IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	260 °C	500 °F	Injection molding
Mold Temperature	80.0 °C	176 °F	Injection molding

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	Active America
Form	Pellets
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
UL.UL-C	Yes