LATI Lastane 50 G/25 PUR, 25% Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced
Manufacturer	LATI
Trade Name	Lastane
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Lastane 50 G/25 PUR, 25% Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polyurethane (PUR) based compound. Glass fibers. Very good noise reduction. Good impact resistance even at low temperature.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.35 g/cc	0.0488 lb/in³
Linear Mold Shrinkage, Flow	0.0025 - 0.0040 cm/cm	0.0025 - 0.0040 in/in
Linear Mold Shrinkage, Transverse	0.0035 - 0.0050 cm/cm	0.0035 - 0.0050 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	45.0 MPa @Temperature 23.0 °C	6530 psi @Temperature 73.4 °F
Elongation at Break	50 % @Temperature 23.0 °C	50 % @Temperature 73.4 °F
Elongation at Yield	35 % @Temperature 23.0 °C	35 % @Temperature 73.4 °F
Tensile Modulus	1.00 GPa @Temperature 23.0 °C	145 ksi @Temperature 73.4 °F
Charpy Impact Unnotched	NB	NB
Charpy Impact, Notched	5.00 J/cm²	23.8 ft-lb/in²

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	165 °C	329 °F

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	600 V	600 V	A solution

Processing Properties	Metric	English
Melt Temperature	200 - 220 °C	392 - 428 °F
Mold Temperature	20.0 - 40.0 °C	68.0 - 104 °F
Drying Temperature	80.0 - 90.0 °C @Time 10800 sec	176 - 194 °F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa