SABIC Innovative Plastics LNP THERMOTUF V1000 PA 66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF V1000 PA 66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOTUF* V1000 is a compound based on Nylon resin. Added features of this material include: High Impact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| 1.073 g/cc | 0.03876 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.800 % | 0.800 % | 50% RH, 24 hrs; ASTM D570 |
| 1.37 % | 1.37 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.013 - 0.015 cm/cm @Time 86400 sec |
0.013 - 0.015 in/in @Time 24.0 hour |
ASTM D955 |
| 0.013 - 0.015 cm/cm @Time 86400 sec |
0.013 - 0.015 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.013 - 0.015 cm/cm @Time 86400 sec |
0.013 - 0.015 in/in @Time 24.0 hour |
ASTM D955 |
| 0.013 - 0.015 cm/cm @Time 86400 sec |
0.013 - 0.015 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527 |
| 50.0 MPa | 7250 psi | ASTM D638 | |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | ISO 527 |
| 45.0 MPa | 6530 psi | ASTM D638 | |
| Elongation at Break | 60.3 % | 60.3 % | ASTM D638 |
| 168.1 % | 168.1 % | ISO 527 | |
| Elongation at Yield | 4.6 % | 4.6 % | ASTM D638 |
| 17.1 % | 17.1 % | ISO 527 | |
| Tensile Modulus | 1.80 GPa | 261 ksi | 1 mm/min; ISO 527 |
| 1.93 GPa | 280 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
| 74.0 MPa | 10700 psi | ASTM D790 | |
| Flexural Modulus | 1.70 GPa | 247 ksi | ISO 178 |
| 1.93 GPa | 280 ksi | ASTM D790 | |
| Izod Impact, Notched (ISO) | 84.0 kJ/m² | 40.0 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 137 kJ/m² | 65.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 56.0 J | 41.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 77.0 J | 56.8 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 127 µm/m-°C @Temperature -40.0 - 40.0 °C |
70.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 127 µm/m-°C @Temperature -40.0 - 40.0 °C |
70.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 126 µm/m-°C @Temperature -40.0 - 40.0 °C |
70.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 126 µm/m-°C @Temperature -40.0 - 40.0 °C |
70.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 53.0 °C @Thickness 3.20 mm |
127 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 670 (NG) Synthetic Oil
- Parker Chomerics CHO-BOND 1069, Part B Silicone Rubber Mixture
- PolyOne Geon™ Vinyl Flexible XV3830 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Cookson Group Plaskon® 440S Mineral Filled Novolac Epoxy Molding Compound (discontinued **)
- 3M Dyneon™ PVDF 1012/1001 Polyvinylidene Fluoride (discontinued **)
- Lord Adhesives 8651 Polymer Resistor Composition
- Plastics Group Polifil® 930L-13GF Glass Fiber-Reinforced Nylon 6 (DAM)
- Lubrizol ESTANE® 5735 Ester Based Thermoplastic Polyurethane (European Grade)
- ExxonMobil Exceed™ 2018KB Metallocene Polyethylene Resin (European Grade)
Copyright © lookpolymers.com All Rights Reserved