DuPont Performance Polymers Delrin® 100T NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced, Impact Grade
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 100T NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Toughened High Viscosity Acetal Homopolymer Delrin 100T NC010 is a toughened high viscosity acetal homopolymer grade with high impact resistance.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
Water Absorption 0.90 %

@Thickness 2.00 mm
 0.90 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.300 %

@Thickness 2.00 mm
 0.300 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 165000 cP

@Shear Rate 5000 1/s,
Temperature 220 °C
 165000 cP

@Shear Rate 5000 1/s,
Temperature 428 °F
 ISO 11403-1 -2
187000 cP

@Shear Rate 5000 1/s,
Temperature 205 °C
 187000 cP

@Shear Rate 5000 1/s,
Temperature 401 °F
 ISO 11403-1 -2
214000 cP

@Shear Rate 5000 1/s,
Temperature 190 °C
 214000 cP

@Shear Rate 5000 1/s,
Temperature 374 °F
 ISO 11403-1 -2
781000 cP

@Shear Rate 500 1/s,
Temperature 220 °C
 781000 cP

@Shear Rate 500 1/s,
Temperature 428 °F
 ISO 11403-1 -2
917000 cP

@Shear Rate 500 1/s,
Temperature 205 °C
 917000 cP

@Shear Rate 500 1/s,
Temperature 401 °F
 ISO 11403-1 -2
1.082e+6 cP

@Shear Rate 500 1/s,
Temperature 190 °C
 1.082e+6 cP

@Shear Rate 500 1/s,
Temperature 374 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.015 cm/cm
0.015 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.016 cm/cm
0.016 in/in
ISO 294-4 2577
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm³/10min; ISO 1133
2.1 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 2.1 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 59
59
ISO 2039-2
Hardness, Rockwell R 113
113
ISO 2039-2
Tensile Stress 8.50 MPa

@Strain 1.60 %,
Temperature 90.0 °C
 1230 psi

@Strain 1.60 %,
Temperature 194 °F
 ISO 11403-1 -2
19.3 MPa

@Strain 6.50 %,
Temperature 90.0 °C
 2800 psi

@Strain 6.50 %,
Temperature 194 °F
 ISO 11403-1 -2
22.0 MPa

@Strain 1.90 %,
Temperature 40.0 °C
 3190 psi

@Strain 1.90 %,
Temperature 104 °F
 ISO 11403-1 -2
22.9 MPa

@Strain 11.4 %,
Temperature 90.0 °C
 3320 psi

@Strain 11.4 %,
Temperature 194 °F
 ISO 11403-1 -2
23.7 MPa

@Strain 16.3 %,
Temperature 90.0 °C
 3440 psi

@Strain 16.3 %,
Temperature 194 °F
 ISO 11403-1 -2
29.0 MPa

@Strain 2.50 %,
Temperature 23.0 °C
 4210 psi

@Strain 2.50 %,
Temperature 73.4 °F
 ISO 11403-1 -2
36.0 MPa

@Strain 2.60 %,
Temperature 0.000 °C
 5220 psi

@Strain 2.60 %,
Temperature 32.0 °F
 ISO 11403-1 -2
40.0 MPa

@Strain 7.60 %,
Temperature 40.0 °C
 5800 psi

@Strain 7.60 %,
Temperature 104 °F
 ISO 11403-1 -2
40.0 MPa

@Strain 2.30 %,
Temperature -20.0 °C
 5800 psi

@Strain 2.30 %,
Temperature -4.00 °F
 ISO 11403-1 -2
44.0 MPa

@Strain 13.3 %,
Temperature 40.0 °C
 6380 psi

@Strain 13.3 %,
Temperature 104 °F
 ISO 11403-1 -2
44.7 MPa

@Strain 21.0 %,
Temperature 40.0 °C
 6480 psi

@Strain 21.0 %,
Temperature 104 °F
 ISO 11403-1 -2
48.7 MPa

@Strain 10.2 %,
Temperature 23.0 °C
 7060 psi

@Strain 10.2 %,
Temperature 73.4 °F
 ISO 11403-1 -2
50.9 MPa

@Strain 17.8 %,
Temperature 23.0 °C
 7380 psi

@Strain 17.8 %,
Temperature 73.4 °F
 ISO 11403-1 -2
51.2 MPa

@Strain 25.4 %,
Temperature 23.0 °C
 7430 psi

@Strain 25.4 %,
Temperature 73.4 °F
 ISO 11403-1 -2
56.1 MPa

@Strain 10.6 %,
Temperature 0.000 °C
 8140 psi

@Strain 10.6 %,
Temperature 32.0 °F
 ISO 11403-1 -2
58.3 MPa

@Strain 18.5 %,
Temperature 0.000 °C
 8460 psi

@Strain 18.5 %,
Temperature 32.0 °F
 ISO 11403-1 -2
58.6 MPa

@Strain 26.4 %,
Temperature 0.000 °C
 8500 psi

@Strain 26.4 %,
Temperature 32.0 °F
 ISO 11403-1 -2
63.9 MPa

@Strain 9.20 %,
Temperature -20.0 °C
 9270 psi

@Strain 9.20 %,
Temperature -4.00 °F
 ISO 11403-1 -2
67.0 MPa

@Strain 16.2 %,
Temperature -20.0 °C
 9720 psi

@Strain 16.2 %,
Temperature -4.00 °F
 ISO 11403-1 -2
67.8 MPa

@Strain 23.1 %,
Temperature -20.0 °C
 9830 psi

@Strain 23.1 %,
Temperature -4.00 °F
 ISO 11403-1 -2
Tensile Strength, Yield 55.0 MPa
7980 psi
ISO 527-1/-2
Elongation at Break >= 50 %
>= 50 %
Nominal; ISO 527-1/-2
Elongation at Yield 25 %
25 %
ISO 527-1/-2
Tensile Modulus 1.90 GPa
276 ksi
ISO 527-1/-2
Flexural Modulus 1.70 GPa
247 ksi
ISO 178
Shear Modulus 0.115 GPa

@Temperature 120 °C
 16.7 ksi

@Temperature 248 °F
 Dynamic; ISO 11403-1 -2
0.262 GPa

@Temperature 70.0 °C
 38.0 ksi

@Temperature 158 °F
 Dynamic; ISO 11403-1 -2
0.514 GPa

@Temperature 20.0 °C
 74.6 ksi

@Temperature 68.0 °F
 Dynamic; ISO 11403-1 -2
0.729 GPa

@Temperature -20.0 °C
 106 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
1.166 GPa

@Temperature -50.0 °C
 169.1 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Secant Modulus 0.252 GPa

@Strain 20.3 %,
Temperature 23.0 °C
 36.5 ksi

@Strain 20.3 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.277 GPa

@Strain 21.1 %,
Temperature 0.000 °C
 40.2 ksi

@Strain 21.1 %,
Temperature 32.0 °F
 ISO 11403-1 -2
0.293 GPa

@Strain 15.2 %,
Temperature 40.0 °C
 42.5 ksi

@Strain 15.2 %,
Temperature 104 °F
 ISO 11403-1 -2
0.365 GPa

@Strain 18.5 %,
Temperature -20.0 °C
 52.9 ksi

@Strain 18.5 %,
Temperature -4.00 °F
 ISO 11403-1 -2
0.477 GPa

@Strain 10.2 %,
Temperature 23.0 °C
 69.2 ksi

@Strain 10.2 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.526 GPa

@Strain 7.60 %,
Temperature 40.0 °C
 76.3 ksi

@Strain 7.60 %,
Temperature 104 °F
 ISO 11403-1 -2
0.529 GPa

@Strain 10.6 %,
Temperature 0.000 °C
 76.8 ksi

@Strain 10.6 %,
Temperature 32.0 °F
 ISO 11403-1 -2
0.695 GPa

@Strain 9.20 %,
Temperature -20.0 °C
 101 ksi

@Strain 9.20 %,
Temperature -4.00 °F
 ISO 11403-1 -2
1.16 GPa

@Strain 1.90 %,
Temperature 40.0 °C
 168 ksi

@Strain 1.90 %,
Temperature 104 °F
 ISO 11403-1 -2
1.16 GPa

@Strain 2.50 %,
Temperature 23.0 °C
 168 ksi

@Strain 2.50 %,
Temperature 73.4 °F
 ISO 11403-1 -2
1.38 GPa

@Strain 2.60 %,
Temperature 0.000 °C
 201 ksi

@Strain 2.60 %,
Temperature 32.0 °F
 ISO 11403-1 -2
1.74 GPa

@Strain 2.30 %,
Temperature -20.0 °C
 252 ksi

@Strain 2.30 %,
Temperature -4.00 °F
 ISO 11403-1 -2
Charpy Impact Unnotched NB
NB
ISO 179/1eU
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 2.50 J/cm²
11.9 ft-lb/in²
ISO 179/1eA
1.30 J/cm²

@Temperature -30.0 °C
 6.19 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 120 µm/m-°C
66.7 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 120 µm/m-°C
66.7 µin/in-°F
ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 130 °C
266 °F
ISO 75-1/-2
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
IEC 60112