Ineos ABS Triax® 1220 S ABS + Polyamide Blend, Extrusion, Conditioned
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon |
| Manufacturer | Ineos ABS |
| Trade Name | Triax® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Triax® 1220 S ABS + Polyamide Blend, Extrusion, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Properties tested in transverse direction (worst case) on 125-mil (3.2 mm) extruded sheets specimens with
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 80 | 80 | ASTM D785 |
| Tensile Strength, Ultimate | 32.0 MPa | 4640 psi | ASTM D638 |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | ASTM D638 |
| Elongation at Break | 90 % | 90 % | ASTM D638 |
| Tensile Modulus | 1.70 GPa | 247 ksi | ASTM D638 |
| Flexural Yield Strength | 61.0 MPa | 8850 psi | at 5% strain; ASTM D790 |
| Flexural Modulus | 1.70 GPa | 247 ksi | ASTM D790 |
| Izod Impact, Notched | 9.00 J/cm @Thickness 3.17 mm |
16.9 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| 1.00 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
1.87 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 | |
| Impact Test | 58.0 J @Thickness 3.20 mm |
42.8 ft-lb @Thickness 0.126 in |
Instrumented Total Impact; 12.5 mm dart, 75 mm clamp, 3.3 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C @Thickness 3.17 mm |
190 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 60.0 °C @Thickness 1.50 mm |
140 °F @Thickness 0.0591 in |
UL746B |
| UL RTI, Mechanical with Impact | 60.0 °C @Thickness 1.50 mm |
140 °F @Thickness 0.0591 in |
UL746B |
| UL RTI, Mechanical without Impact | 60.0 °C @Thickness 1.50 mm |
140 °F @Thickness 0.0591 in |
UL746B |
| Flammability, UL94 | HB @Thickness 1.57 mm |
HB @Thickness 0.0618 in |
White color |
| HB @Thickness 1.57 mm |
HB @Thickness 0.0618 in |
White color |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 9.00e+12 ohm-cm | 9.00e+12 ohm-cm | Tinfoil Electrodes; ASTM D257 |
| Surface Resistance | 3.20e+13 ohm | 3.20e+13 ohm | ASTM D257 |
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 15.0 kV/mm @Thickness 1.60 mm |
381 kV/in @Thickness 0.0630 in |
Short time under oil; ASTM D149 |
| Dissipation Factor | 0.039 @Frequency 1e+6 Hz |
0.039 @Frequency 1e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Momentive Performance Materials Siloprenâ„¢ LSR 2620 Liquid Silicone Rubber - Fast Cure / High Tear
- Multibase Multi-Flamâ„¢ 2602 PP Polypropylene
- SABIC Innovative Plastics NORYL WCP921A PPE-TPE
- SABIC Innovative Plastics LNP THERMOCOMP 2C003 ETFE
- Chesterton ARC 5ES Rapid Repair Stick
- Dow AFFINITY™ SM 8250 Polyolefin Plastomer
- Hippe PF CC 32 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod
- Akzo Nobel Trigonox® EHP-W40S Polymerization Initiator
- Arlon Thermavac® 0.040" (0.762 mm) Cured Silicone Vacuum Bagging (10502R040)
- NOVA Chemicals Sclair® 35BPM MDPE Extrusion Resin, 2.2% Carbon Black Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved