A. Schulman FORMION™ FI 232H 10% Mineral Reinforced Ionomer / Nylon Alloy

Category	Polymer , Thermoplastic , Ionomer , Nylon
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	A. Schulman FORMION™ FI 232H 10% Mineral Reinforced Ionomer / Nylon Alloy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

DescriptionFormion® FI 232H is an injection molding grade, 10% mineral reinforced Ionomer / Nylon alloy, which has been formulated for high scratch resistance, high stiffness and exceptional impact. ApplicationFormion® FI 232H is targeted for non painted, mold-in-color, exterior or interior appearance applications.Information provided by A. Schulman.

Physical Properties	Metric	English	Comments
Specific Gravity	1.09 g/cc	1.09 g/cc	ISO 1183/1
Linear Mold Shrinkage	0.0010 - 0.0060 cm/cm @Thickness 3.20 mm	0.0010 - 0.0060 in/in @Thickness 0.126 in	72 hr; ISO 294
	0.0011 - 0.0070 cm/cm @Thickness 3.20 mm	0.0011 - 0.0070 in/in @Thickness 0.126 in	aged 48 hrs at 121°C; ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	38.0 MPa	5510 psi	ISO 527
Elongation at Break	325 %	325 %	ISO 527
Flexural Modulus	1.70 GPa	247 ksi	Tangent; ISO 178
Izod Impact, Notched (ISO)	65.0 kJ/m²	30.9 ft-lb/in²	pb; ISO 180

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	102 °C @Thickness 3.20 mm	216 °F @Thickness 0.126 in	ISO 75

Users viewing this material also viewed the following: