Cresset Powers Cress-Alon™ A3000 3.0 r.v. Film or Extrusion Grade Nylon 6, 50% RH
| Category | Polymer , Film , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Cresset Powers, Ltd |
| Trade Name | Cress-Alon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cresset Powers Cress-Alon™ A3000 3.0 r.v. Film or Extrusion Grade Nylon 6, 50% RH.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Neat resin, for film or extrusion.Information provided by Cresset Powers Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 - 1.14 g/cc | 0.0405 - 0.0412 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | circa |
| Viscosity Measurement | 2.95 - 3.05 | 2.95 - 3.05 | Relative Viscosity |
| Melt Flow | 17.3 g/10 min @Load 2.16 kg, Temperature 230 °C |
17.3 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | ASTM D638 |
| Elongation at Yield | 7.6 % | 7.6 % | ASTM D638 |
| Flexural Yield Strength | 78.0 MPa | 11300 psi | ASTM D790 |
| Flexural Modulus | 1.70 GPa | 247 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 224 °C | 435 °F | ASTM DSC |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Content | <= 0.10 % | <= 0.10 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Extractables, wt% | <0.5 |
Users viewing this material also viewed the following:
- Huntsman MY 9512 Multifunctional Resin
- Solvay Specialty Polymers Catalyst PS/2LR Polyolefin
- A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT
- A. Schulman POLYFORT™ FPP 3711 High Impact Polypropylene
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 70A, Non-Black Sulfur Cure
- ExxonMobil LDPE LD 156BW Low Density Polyethylene Resin
- ChevronTexaco Cetus® PAO 43
- Arkema Group Rilsan® BZM 30 TL Nylon 11, 30% Glass Fiber Filled (Dry)
- Ashley Polymers Ashlene® 830LS-33G Nylon 6, 33% Glass Reinforced
- Techmer ES Electrablend® PA6 CF20 BK 20% Carbon Filled
Copyright © lookpolymers.com All Rights Reserved