SABIC Innovative Plastics Noryl RF1132 PPE+PP
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl RF1132 PPE+PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PP blend for high frequency applications. Good heat resistance and low DK.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.970 g/cc | 0.970 g/cc | ASTM D 792 |
| Density | 0.970 g/cc | 0.0350 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.020 % | 0.020 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.060 % @Temperature 23.0 °C |
0.060 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.012 cm/cm @Thickness 3.20 mm |
0.0080 - 0.012 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 10.6 g/10 min @Load 5.00 kg, Temperature 260 °C |
10.6 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D 1238 |
| 11 g/10 min @Load 5.00 kg, Temperature 260 °C |
11 g/10 min @Load 11.0 lb, Temperature 500 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 32.0 MPa | 4640 psi | Type I, 50 mm/min; ASTM D 638 |
| 33.0 MPa | 4790 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 50 mm/min; ISO 527 |
| 35.0 MPa | 5080 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | 170 % | 170 % | 50 mm/min; ISO 527 |
| 195 % | 195 % | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Yield | 2.6 % | 2.6 % | 50 mm/min; ISO 527 |
| 6.5 % | 6.5 % | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Modulus | 1.34 GPa | 194 ksi | 50 mm/min; ASTM D 638 |
| 1.50 GPa | 218 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 50.0 MPa | 7250 psi | 2 mm/min; ISO 178 |
| 51.0 MPa | 7400 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 1.55 GPa | 225 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 1.70 GPa | 247 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.49 J/cm @Temperature -30.0 °C |
2.79 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 4.37 J/cm @Temperature 23.0 °C |
8.19 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 37.0 J @Temperature 23.0 °C |
27.3 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 81.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 90.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 112 µm/m-°C @Temperature -40.0 - 40.0 °C |
62.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 120 µm/m-°C @Temperature 23.0 - 60.0 °C |
66.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C @Thickness 3.20 mm |
235 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 77.0 °C @Thickness 3.20 mm |
171 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 95.0 °C | 203 °F | Rate B/50; ISO 306 |
| 100 °C | 212 °F | Rate B/120; ISO 306 | |
| 138 °C | 280 °F | Rate B/50; ASTM D 1525 | |
| Flammability, UL94 | HB @Thickness 1.52 mm |
HB @Thickness 0.0598 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.2 @Frequency 1.00e+6 Hz |
2.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.2 @Frequency 50.0 - 60.0 Hz |
2.2 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| 2.38 @Frequency 1.20e+9 Hz |
2.38 @Frequency 1.20e+9 Hz |
ASTM D 2520 - Mth B | |
| 2.39 @Frequency 1.00e+10 Hz |
2.39 @Frequency 1.00e+10 Hz |
ASTM D 2520 - Mth B | |
| 2.42 @Frequency 2.40e+9 Hz |
2.42 @Frequency 2.40e+9 Hz |
ASTM D 2520 - Mth B | |
| Dielectric Strength | 22.0 kV/mm @Thickness 3.20 mm |
559 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0010 @Frequency 1.00e+6 Hz |
0.0010 @Frequency 1.00e+6 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- PolyOne OnForce™ LFT UR-40 LGF/000 Natural Polyurethane, Unspecified (PUR, Unspecified)
- Polimeri Europa Clearflex® CH G0 Very Low Density Polyethylene
- DSM Somos® 9120 Epoxy Photopolymer (Unverified Data**)
- Lord Adhesives Thermosetâ„¢ SC-303 Silicone Encapsulant, Flame Retardant
- SABIC Innovative Plastics LNP STAT-KON DC10EPFR PC
- Saint-Gobain COHRlastic® CF3320 Reinforced Solid Rubber
- ConocoPhillips Tacna® Rx NLGI No. 1
- Akro-Plastic Akromid® B3 (2500) PA 6 Dry
- EMS-Grivory Grivory® GV-6H PA*-GF60
Copyright © lookpolymers.com All Rights Reserved