SABIC Innovative Plastics LNP Thermocomp MK001AS PP (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp MK001AS PP (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* MK001AS is a compound based on Polypropylene resin containing Mineral. Added features include: Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ISO 1183 |
| Water Absorption | 0.070 % @Temperature 23.0 °C, Time 86400 sec |
0.070 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 34 % | 34 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 5.2 % | 5.2 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 1.60 GPa | 232 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 41.0 MPa | 5950 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.70 GPa | 247 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 140 µm/m-°C @Temperature 23.0 - 60.0 °C |
77.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 145 µm/m-°C @Temperature 23.0 - 60.0 °C |
80.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Old Hickory M-44 Kentucky Ball Clay
- LyondellBasell Petrothene® NA870252 Low Density Polyethylene
- SABIC Innovative Plastics LNP STAT-KON DD0009P PC (Asia Pacific)
- Techmer ES Plastiblend® PC/PBT IM 5727 BK
- Samsung Cheil Industries Starex® HR-0370F ABS, Unreinforced Heat Resistant
- Teknor Apex Elexar® EL 1934C Thermoplastic Elastomer
- ExxonMobil 32 Mobiltemp SHC Series
- Diamond Polymers ASA TWP 121
Copyright © lookpolymers.com All Rights Reserved