Inno-Comp INNOPOL® CS 2-2523 EP 16% Talc Filled, Elastomer Modified Polypropylene Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 2-2523 EP 16% Talc Filled, Elastomer Modified Polypropylene Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 2-2523 EP is a 16% talc-filled, elastomer modified compound based on polypropylene block-copolymer. This grade is available in natural and custom colored form.INNOPOL® CS 2-2523 EP is developed for producing injection molded automotive components.Information provided by INNO-COMP
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | ISO 1183 |
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 230 °C |
18 g/10 min @Load 4.76 lb, Temperature 446 °F |
nozzle diam 2.095 mm; ISO 1133 |
| Storage Temperature | <= 60.0 °C | <= 140 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 21.0 MPa | 3050 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 1.60 GPa | 232 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 1.70 GPa | 247 ksi | ISO 178 |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -20.0 °C |
2.86 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eA |
| 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | ISO 75-1,-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 240 °C | 374 - 464 °F | Injection |
| Middle Barrel Temperature | 190 - 240 °C | 374 - 464 °F | Injection |
| Front Barrel Temperature | 190 - 240 °C | 374 - 464 °F | Injection |
| Melt Temperature | 210 - 250 °C | 410 - 482 °F | Injection |
| Mold Temperature | 15.0 - 50.0 °C | 59.0 - 122 °F | |
| Moisture Content | <= 0.070 % | <= 0.070 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Designation | PP/PE TD 16 | ISO 1043 |
Users viewing this material also viewed the following:
- Polykemi AB POLYshine PBT D221 Q25 PBT, Mineral Reinforced
- Lehmann & Voss LUVOCOM® 1-1119 VP Polyamide 66, with carbon fiber, heat stabilized
- Teknor Apex Telcar® TL-1522E Thermoplastic Elastomer
- Wellman Wellamid® MR409 22H-N 40% Mineral Reinforced Nylon 66, Heat Stabilized
- A. Schulman POLYPUR™ FPU 1376 Thermoplastic Polyurethane Compound
- A. Schulman POLYBATCH™ Cream 90059 Concentrate Based In Polyethylene
- China Tungsten K520 Tungsten Carbide for Mining Purposes
- ExxonMobil Mobil Pyrogard 53
- Bapolene® 2040 Polyethylene, Blow Molding
- BASF Octadecyl Vinyl Ether
Copyright © lookpolymers.com All Rights Reserved