Lehmann & Voss LUVOCOM® 1800-8435 PET, with PTFE
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1800-8435 PET, with PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteristics.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.61 g/cc | 1.61 g/cc | ISO 1183 |
| Water Absorption | <= 0.30 % | <= 0.30 % | 23°C/24h |
| Linear Mold Shrinkage | 0.015 - 0.020 cm/cm | 0.015 - 0.020 in/in | |
| Melt Flow | <= 16.1 g/10 min @Load 1.20 kg, Temperature 280 °C |
<= 16.1 g/10 min @Load 2.65 lb, Temperature 536 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 35.0 MPa | 5080 psi | |
| Elongation at Yield | 2.4 % | 2.4 % | |
| 3.0 % | 3.0 % | flexural | |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | |
| Flexural Strength | 55.0 MPa | 7980 psi | |
| Flexural Modulus | 1.70 GPa | 247 ksi | |
| Charpy Impact Unnotched | 1.50 J/cm² | 7.14 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| 180 °C | 356 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 280 °C | 536 °F | mass temp |
| Nozzle Temperature | 265 - 275 °C | 509 - 527 °F | |
| Zone 1 | 285 - 295 °C | 545 - 563 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 265 - 275 °C | 509 - 527 °F | |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | |
| Drying Temperature | 80.0 °C @Time 21600 - 28800 sec |
176 °F @Time 6.00 - 8.00 hour |
|
| 120 °C @Time 7200 - 18000 sec |
248 °F @Time 2.00 - 5.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (white) |
Users viewing this material also viewed the following:
- Omya OMYACARB® 3 - AZ Calcium Carbonate
- Ineos ABS NOVODUR® KU 2-5300 ABS, Injection Grade (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-8002 PEEK, with carbon fiber
- Sumitomo Chemical ESPOLEX® WT487X Thermoplastic Elastomer
- Von Roll Isola IMI Irrathene® 210 Irradiated Polyethylene Film, Encapsulation Grade
- Wellman Wellamid® MRGF25/15 42H-BKDX9 Nylon 6, 25% Mineral and 15% Glass Fiber Reinforced
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 0.0 PHR MBT
- Axiall 3802 Vinyl Foam, Extrusion
- Abatron AboCast 8103-23 High-Performance Dielectric Epoxy
- Plaslok 5303 Black Electrical Grade Mineral/Flock Filled Phenolic Molding Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved