Ineos ABS TRIAX® 1220 S ABS/Nylon Blend, As Conditioned
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon |
| Manufacturer | Ineos ABS |
| Trade Name | Triax® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS TRIAX® 1220 S ABS/Nylon Blend, As Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Extrusion and injection molding grade with good stress corrosion cracking resistance, good chemical resistance (fuel, cleaning agents), high impact and notched impact strength, good acoustical damping behavior.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | Dry As Molded |
| Linear Mold Shrinkage | 0.0045 cm/cm | 0.0045 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 69 | 69 | ASTM D785 |
| Tensile Strength, Ultimate | 32.0 MPa | 4640 psi | ASTM D638 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | |
| Elongation at Break | 90 % | 90 % | ASTM D638 |
| Elongation at Yield | 11 % | 11 % | |
| Tensile Modulus | 0.900 GPa | 131 ksi | |
| Flexural Yield Strength | 61.0 MPa | 8850 psi | at 5% strain; ASTM D790 |
| Flexural Modulus | 1.70 GPa | 247 ksi | ASTM D790 |
| Izod Impact, Notched | 9.00 J/cm @Thickness 3.20 mm |
16.9 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| 1.00 J/cm @Thickness 3.20 mm, Temperature -40.0 °C |
1.87 ft-lb/in @Thickness 0.126 in, Temperature -40.0 °F |
ASTM D256 | |
| Charpy Impact Unnotched | NB | NB | |
| 2.30 J/cm² @Temperature -30.0 °C |
10.9 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 7.00 J/cm² | 33.3 ft-lb/in² | |
| Impact Test | 61.0 J @Thickness 3.20 mm |
45.0 ft-lb @Thickness 0.126 in |
Instrumented Total Impact; 3.2 mm thick, 12.5 mm dart, 75 mm clamp, 3.3 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C | 205 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | |
| Vicat Softening Point | 94.0 °C | 201 °F | |
| UL RTI, Electrical | 60.0 °C | 140 °F | |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 9.00e+12 ohm-cm | 9.00e+12 ohm-cm | ASTM D257 |
| Surface Resistance | 3.20e+13 ohm | 3.20e+13 ohm | ASTM D257 |
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 15.0 kV/mm @Thickness 1.60 mm |
381 kV/in @Thickness 0.0630 in |
Short time under oil; ASTM D149 |
| Dissipation Factor | 0.039 @Frequency 1e+6 Hz |
0.039 @Frequency 1e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- REXtac Rextac® RT 2535 Amorphous Polyalphaolefin (APAO)
- Nilit Polynil® P60 Medium Viscosity Nylon 66
- Polimeri Europa SINKRAL PD M323 ABS (discontinued **)
- Overview of materials for PVC, Transparent
- Mitsubishi Iupilon® H2000UR 23 MFI, UV Stabilized Polycarbonate With Release
- Lavergne VYPET VNT 645 PET 45% Glass Reinforced
- Samsung Cheil Industries Starex® SR-0305 ABS, Unreinforced Heat Resistant
- Solvay RHODACAL® 60/B Surfactant
- ExxonMobil Exceed™ 2018EB Metallocene Polyethylene Resin (European Grade)
- Aclo Accutech Polypropylene Homopolymer HP0334G25M5CL Glass/Mineral Reinforced Coupled
Copyright © lookpolymers.com All Rights Reserved