Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 9.45 GPa | 1370 ksi | ASTM D790 |
Ravago Manufacturing Americas Hylon® N2033HL Nylon 6 (DAM) Information provided by Ravago. |
|||
Flexural Modulus | 9.45 GPa | 1370 ksi | ASTM Value |
BASF Capron® HPN 9233G 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron HPN 9233G is a 33% glass reinforced polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface aesthetics. It is.. |
|||
Flexural Modulus | 9.47 GPa | 1370 ksi | ASTM D790 |
Plenco 7466 Phenolic, Granular, Transfer Molded
(discontinued **) Two-Stage Phenolic. PLENCO 07466 is a flock cotton and mineral filled phenolic molding compound offering excellent heat resistance and dimensional stability. UL recognized under component file E406.. |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | ASTM D 790 |
SABIC Innovative Plastics LNP Stat-kon DEF13 PC LNP* Stat-kon* DEF13 is a compound based on Polycarbonate resin containing Glass Fiber, Glass Fiber, Carbon Fiber. Added features of this material include: Electrically Conductive.This data was sup.. |
|||
Flexural Modulus | 9.41 GPa | 1370 ksi | ASTM D790 |
Shinkong Synthetic Fibers Shinite® T101G30 PET, 30% Glass Filled Information from Shinkong Synthetic Fibers Corp. |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP AFB42 ABS LNP* THERMOCOMP* AFB42 is a compound based on ABS containing 10% Glass Fiber, 20% Glass Bead. |
|||
Flexural Modulus | 9.45 GPa | 1370 ksi | ASTM D790 |
Techmer ES Plaslube® J-1/30/TF/13/SI/2 NAT PA66 |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF006H PA 66 LNP THERMOCOMP* RF006H is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
Flexural Modulus | 9.48 GPa | 1370 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP RF006I PA 66 LNP* THERMOTUF* RF006I is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: High Impact. |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF006XXZ PA 66 LNP THERMOCOMP* RF006XXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP RF007H PA 66 LNP* Thermocomp* RF007H is a compound based on Nylon 66 containing glass fiber. Added feature includes: Healthcare. |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP RF007SXP PA 66 LNP* THERMOCOMP* RF007SXP is a compound based on Nylon 66 containing 35% Glass Fiber. Added feature of this material includes: Heat Stabilized. |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RX02743 PA 66 LNP* Thermocomp* RX02743 is a compound based on Nylon 66 resin containing Glass Fiber. |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RX02743 PA 66 (Asia Pacific) LNP* Thermocomp* RX02743 is a compound based on Nylon 66 resin containing Glass Fiber. |
|||
Flexural Modulus | 9.48 GPa | 1370 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP RX06421S PA 66 LNP* Thermocomp* RX06421S is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Easy Molding. |
|||
Flexural Modulus | 9.41 GPa | 1370 ksi | ASTM D790 |
Shinkong Synthetic Fibers Shinite® T101G30 PET, 30% Glass Filled Information from Shinkong Synthetic Fibers Corp. |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP WF006H PBT LNP* THERMOCOMP* WF006H is a compound based on PBT resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
Flexural Modulus | 9.48 GPa | 1370 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOTUF RF006I PA 66 LNP* Thermotuf* RF006I is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: High Impact. |
|||
Flexural Modulus | 9.48 GPa | 1370 ksi | ISO 178 |
SABIC Innovative Plastics LNP Thermotuf RF006I PA 66 LNP* Thermotuf* RF006I is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: High Impact.This data was supplied by SABIC-IP for the Americas region... |
|||
Flexural Modulus | 9.45 GPa | 1370 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® SHF4960 PBT (Europe-Africa-Middle East) Valox Super high flow grade, 30% glass filled Flame retardant, High CTI, heat stabilized with mold release. |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP WF006H PBT (Asia Pacific) LNP* Thermocomp* WF006H is a compound based on Polybutylene Terephalate resin containing Glass Fiber. |
|||
Flexural Modulus | 9.47 GPa | 1370 ksi | ISO 178 |
Polyplastics Duranex® 7390W Polybutylene Terephthalate (PBT), Super low warpage, GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Flexural Modulus | 9.45 GPa | 1370 ksi | DAM; ISO 178 |
DuPont Performance Polymers Zytel® FR50 NC010A Nylon 66
(Unverified Data**) 25% Glass Reinforced Flame Retardant Polyamide 66 Zytel FR50 NC010A is a 25% glass fiber reinforced flame retardant polyamide 66 resin for injection molding.Information provided by DuPont Performanc.. |
|||
Flexural Modulus | 9.41 GPa | 1370 ksi | 2.8mm/min; ASTM D790 |
Asia International Enterprise (Hong Kong) 60G6-33GF Nylon 66, 33% Filled Information provided by Asia International Enterprise (Hong Kong) Ltd. |
|||
Flexural Modulus | 9.43 GPa | 1370 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Verton MV00ASUV_WH9D703 PP Preliminary data for 50% Long fiber single color pellet filled PPThis data was supplied by SABIC-IP for the Americas region. |