SABIC Innovative Plastics LNP THERMOCOMP AFB42 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP AFB42 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* AFB42 is a compound based on ABS containing 10% Glass Fiber, 20% Glass Bead.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ASTM D792 |
| 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.110 % | 0.110 % | 50% RH, 24 hrs; ASTM D570 |
| 0.110 % | 0.110 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Time 86400 sec |
0.0040 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm @Time 86400 sec |
0.0050 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.0 MPa | 6960 psi | 5 mm/min; ISO 527 |
| 51.0 MPa | 7400 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | 5 mm/min; ISO 527 |
| 28.0 MPa | 4060 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.2 % | 1.2 % | Type I, 5 mm/min; ASTM D638 |
| 1.7 % | 1.7 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.75 GPa | 689 ksi | 1 mm/min; ISO 527 |
| 9.40 GPa | 1360 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 76.0 MPa | 11000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.92 GPa | 714 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 9.44 GPa | 1370 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 2.90 J/cm | 5.43 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 0.720 J/cm | 1.35 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | 80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 102 °C @Thickness 3.20 mm |
216 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 95.0 °C @Thickness 3.20 mm |
203 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 79 T 20 PP/C reinforced with 20% mineral filler
- Nye Lubricants 708C (NG) Synthetic Oil
- Lanxess Durethan® AKV 35 CX H2.0 900876 Nylon 66, Glass Fiber Reinforced
- Silberline "A" Series A-1592FG
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 60 PHR Hi-Sil 243 LD Filler
- Trelleborg B473 Nitrile Rubber
- Aremco Aremco-Bond™ 820 High Performance Epoxide
- Braskem CP 405 XP Injection Molding Polypropylene
- Teijin Panlite® GV-3410R High Flame Retardancy, Glass Fiber Reinforced Polycarbonate Resin
Copyright © lookpolymers.com All Rights Reserved