SABIC Innovative Plastics LNP THERMOCOMP RF007H PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF007H PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RF007H is a compound based on Nylon 66 containing glass fiber. Added feature includes: Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.730 % | 0.730 % | 50% RH, 24 hrs; ASTM D570 |
| 1.00 % | 1.00 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Time 86400 sec |
0.0020 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 185 MPa | 26800 psi | Type I, 5 mm/min; ASTM D638 |
| 185 MPa | 26800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 |
| 2.6 % | 2.6 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 11.17 GPa | 1620 ksi | 1 mm/min; ISO 527 |
| 11.38 GPa | 1651 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 249 MPa | 36100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 266 MPa | 38600 psi | ISO 178 | |
| Flexural Yield Strength | 250 MPa | 36300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 8.10 GPa | 1170 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 9.44 GPa | 1370 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.780 J/cm | 1.46 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.88 J/cm | 14.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 73.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
40.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID® 66 GF 20 HTS PA6 reinforced with glass fiber, heat stabilized, hydrolysis resistant
- PTS PCA-1010HF High Flow Polycarbonate/ABS Alloy
- LyondellBasell Petrothene® LR734001 High Density Polyethylene (Blow Molding Grade)
- Gouda Vuurvast CURON 150 AC Dense Refractory Castable
- Amity Thermosets ATS 132 Phenolic Molding Organic, inorganic, and graphite Filler, Compression Molded
- Borealis ME268Al Polypropylene Compound, Mineral Filled
- LG Chemical HYPERIER IP1106 PA-PE Nanoclay Compound
- Ineos Nova 5504 High Impact Polystyrene (discontinued **)
- Fainplast Compounds PM 80/R1 Flexible PVC, Lead Free
Copyright © lookpolymers.com All Rights Reserved