- SABIC Innovative Plastics LNP Stat-kon DEF13 PC
SABIC Innovative Plastics LNP Stat-kon DEF13 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon DEF13 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* DEF13 is a compound based on Polycarbonate resin containing Glass Fiber, Glass Fiber, Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D 792 |
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D 792 |
| 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 | |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D 570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 12.0 MPa | 1740 psi | 5 mm/min; ISO 527 |
| 118 MPa | 17100 psi | ASTM D 638 | |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | 5 mm/min; ISO 527 |
| 61.0 MPa | 8850 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| 4.0 % | 4.0 % | ASTM D 638 | |
| Tensile Modulus | 12.41 GPa | 1800 ksi | 1 mm/min; ISO 527 |
| 17.87 GPa | 2592 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 159 MPa | 23100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 211 MPa | 30600 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 9.44 GPa | 1370 ksi | ASTM D 790 |
| 18.5 GPa | 2680 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.960 J/cm @Temperature 23.0 °C |
1.80 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.13 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
9.61 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 148 °C | 298 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 144 °C | 291 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 144 °C @Thickness 3.20 mm |
291 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- Nye Lubricants 132G (SO) Synthetic Oil
- Nylene® Vexel™ B50U , High Flow, Un-reinforced PBT
- Custom Resins Vexel™ E20GF30 , 30% Glass Reinforced PET (discontinued **)
- NOVA Chemicals DYLARK® 250 Impact Grade Engineering Resin
- Special Metals Electroformed Nickel, 200 Micron (8 mil) Foil, Electroformed and Annealed
- Samsung Cheil Industries Starex® EA-0640 ABS, Unreinforced
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 20 PHR N774 (SRF) Filler
- Chicago Extruded Metals BioBrass® UNS C62500 Aluminum Bronze
- Bhansali Engineering Abstron KU670 ABS Heat Resistant
- 3M FV022702 White Vinyl Label Products
Copyright © lookpolymers.com All Rights Reserved