SABIC Innovative Plastics LNP THERMOCOMP RF006I PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF006I PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOTUF* RF006I is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: High Impact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.630 % | 0.630 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0027 cm/cm @Time 86400 sec |
0.0027 in/in @Time 24.0 hour |
ISO 294 |
| 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0112 cm/cm @Time 86400 sec |
0.0112 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 161 MPa | 23400 psi | ASTM D638 |
| 179 MPa | 26000 psi | ISO 527 | |
| Elongation at Break | 2.9 % | 2.9 % | ISO 527 |
| 3.2 % | 3.2 % | ASTM D638 | |
| Tensile Modulus | 10.41 GPa | 1510 ksi | 50 mm/min; ASTM D638 |
| 10.84 GPa | 1572 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 248 MPa | 36000 psi | ASTM D790 |
| 266 MPa | 38600 psi | ISO 178 | |
| Flexural Modulus | 8.68 GPa | 1260 ksi | ASTM D790 |
| 9.48 GPa | 1370 ksi | ISO 178 | |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.21 J/cm | 21.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² | 35.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 17.0 J | 12.5 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 27.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 60.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 60.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 126 °C @Thickness 3.20 mm |
259 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C @Thickness 3.20 mm |
250 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Reltek SEALiT™ A-46 Clear Coat & Sealant
- A. Schulman POLYBATCH™ White HS8350 Concentrate Based In Impact Polystyrene
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 290ºF Cure Temperature
- Diamond Polymers NPP20-1201CAS Random Copolymer Polypropylene (Clarified, with Antistat)
- China Tungsten ZM10-1 Tungsten Carbide
- Axiall 2192 Wire & Cable Flexible PVC
- Gharda Chemicals GAFONE™ 3420GF PES, Glass Fiber-Reinforced (discontinued **)
Copyright © lookpolymers.com All Rights Reserved