BASF Capron® HPN 9233G 33% Glass-Filled Nylon 6 (Dry)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® HPN 9233G 33% Glass-Filled Nylon 6 (Dry)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Capron HPN 9233G is a 33% glass reinforced polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface aesthetics. It is one of the High Productivity Nylon series products, offering the performance characteristics of a premium glass fiber reinforced polyamide while reducing cycle time and improving surface appearance. It is also available in heat stabilized (Capron HPN 9233G HS) and/or pigmented versions.Capron HPN 9233G is generally recommended for high performance applications such as window locks, valve bodies, chair shells, door and window hardware, connectors, switch components, relay parts, terminal blocks, power tool housings, gears, chain saws, blowers, and trimmer housings.Data provided by Allied Signal.Processing: Max. water content 0.12%. Product is supplied in sealed containers and drying is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 85°C (185 °F). Is recommended. Drying time is dependent on moisture level.Melt Temperature: 270-295 degC (518-563 degF). Mold Temperature: 80-95 degC (176-203 degF). Injection and Packing Pressure: 35-125 bar (500-1500psi) This product can be processed over a wide range of mold temperatures; however, for applications where aesthetics critical, a mold surface temperature of 80-95 degC (176-203 degF) is required. Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off. Back pressure can be utilized to provide uniform melt consistency and reduce trapped air and gas. A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate. Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
ISO data
Water Absorption 1.1 %
1.1 %
24 hrs; ISO data
Moisture Absorption at Equilibrium 1.8 %
1.8 %
50% RH; 23°C; ISO data
Water Absorption at Saturation 6.4 %
6.4 %
in water; 23°C; ISO data
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM Data MD
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 185 MPa
26800 psi
Same value from ASTM and ISO tests; 5 mm/min.
Elongation at Break 3.0 %
3.0 %
ISO, 5 mm/minl
3.0 %
3.0 %
ASTM, 5 mm/minl
Tensile Modulus 11.17 GPa
1620 ksi
same value from ASTM and ISO test.
Flexural Yield Strength 295 MPa
42800 psi
ASTM Data
Flexural Modulus 8.40 GPa
1220 ksi
ISO Value
9.45 GPa
1370 ksi
ASTM Value
Poissons Ratio 0.35
0.35
ISO data
Shear Modulus 4.10 GPa
595 ksi
calculated
Charpy Impact, Notched 1.30 J/cm²
6.19 ft-lb/in²
ISO Data
1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
ISO data
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 21.0 µm/m-°C

@Temperature 20.0 °C
11.7 µin/in-°F

@Temperature 68.0 °F
ISO data
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature 20.0 °C
38.9 µin/in-°F

@Temperature 68.0 °F
ISO data
Melting Point 220 °C
428 °F
ASTM and ISO test
Deflection Temperature at 0.46 MPa (66 psi) 218 °C
424 °F
ISO data
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ISO data
207 °C
405 °F
ASTM Data
Flammability, UL94 HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ISO data
Processing Properties Metric English Comments
Processing Temperature 275 °C
527 °F
See Materials Notes
Mold Temperature 95.0 °C
203 °F
See Materials Notes
Drying Temperature 85.0 °C
185 °F
See Materials Notes