SABIC Innovative Plastics LNP THERMOCOMP RF006H PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF006H PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* RF006H is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.690 % | 0.690 % | 50% RH, 24 hrs; ASTM D570 |
| 1.20 % | 1.20 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D955 |
| 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 154 MPa | 22300 psi | 5 mm/min; ISO 527 |
| 165 MPa | 23900 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.4 % | 2.4 % | Type I, 5 mm/min; ASTM D638 |
| 2.4 % | 2.4 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 8.98 GPa | 1300 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 235 MPa | 34100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 9.22 GPa | 1340 ksi | 2 mm/min; ISO 178 |
| 9.44 GPa | 1370 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.46 J/cm | 12.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 52.0 kJ/m² | 24.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J | 4.43 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.71 | 0.71 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.57 | 0.57 | ASTM D3702 Modified |
| K (wear) Factor | 151 x 10-8 mm³/N-M | 75.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 30.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 73.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 73.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 265 °C @Thickness 3.20 mm |
509 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 243 °C | 469 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 255 °C @Thickness 3.20 mm |
491 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Molding M5700 Natural Polyvinyl Chloride, Rigid (PVC, Rigid)
- SABIC Innovative Plastics Lexan® SLX2531T PC Copolymer (Europe-Africa-Middle East)
- LG Chemical LUPOS GP-2200H General Purpose ABS, 20% Glass Fiber Reinforced, High Heat Resistance
- SABIC Innovative Plastics Ultem DT1800E PEI Blend (Asia Pacific)
- Polyram PlusTek PA313G43 Nylon 66 for Injection Molding, 43% Glass Fiber Reinforced, Heat Stabilized
- Wellman Wellamid® FRGF1850-BK1 Nylon 66, 25% Glass Fiber Reinforced, Flame Retardant
- Loctite® 3566 Rapid Flow Low Profile Underfill
- 3M 301+ Performance Yellow Masking Tape
- Braskem FT120WB2 Homopolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved