SABIC Innovative Plastics LNP THERMOTUF RF006I PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF RF006I PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermotuf* RF006I is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: High Impact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.630 % | 0.630 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0027 cm/cm @Time 86400 sec |
0.0027 in/in @Time 24.0 hour |
ISO 294 |
| 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0112 cm/cm @Time 86400 sec |
0.0112 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 161 MPa | 23400 psi | ASTM D638 |
| 179 MPa | 26000 psi | ISO 527 | |
| Elongation at Break | 2.9 % | 2.9 % | ISO 527 |
| 3.2 % | 3.2 % | ASTM D638 | |
| Tensile Modulus | 10.41 GPa | 1510 ksi | 50 mm/min; ASTM D638 |
| 10.84 GPa | 1572 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 248 MPa | 36000 psi | ASTM D790 |
| 266 MPa | 38600 psi | ISO 178 | |
| Flexural Modulus | 8.68 GPa | 1260 ksi | ASTM D790 |
| 9.48 GPa | 1370 ksi | ISO 178 | |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.21 J/cm | 21.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² | 35.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 17.0 J | 12.5 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 27.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 60.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 60.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C @Thickness 3.20 mm |
498 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C @Thickness 3.20 mm |
250 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1105/CF/10/GR/10/TF/10-2 PEEK, with carbon fiber, PTFE, lubricant modified
- Taiwan Sheen Soon Sheenthane® A8521H TPU for Ink
- NAPCO F96 - Fused Magnesia
- A. Schulman POLYFORT™ FPP 1236-2939 Fiberglass Reinforced Homopolymer Polypropylene
- Plenco 6527 Phenolic, Granular, Transfer Molded
- Lubrizol Estane® R175A Thermoplastic Polyurethane
- DSM Akulon® K222-KMV5 Nylon 6-25% Mineral Reinforced (European and Asian Grade) (Cond)
- ExxonMobil 526 Mobil SHC 500 Series
- Haynes 230® alloy plate, 8000 hours exposure at 649°C (1200°F)
- Schmolz + Bickenbach Formadur® 2316/2316 ESR Plastic Mold Steel
Copyright © lookpolymers.com All Rights Reserved