Techmer ES Plaslube® J-1/30/TF/13/SI/2 NAT PA66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Techmer ES |
| Trade Name | Plaslube® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Plaslube® J-1/30/TF/13/SI/2 NAT PA66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | 24 Hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength at Break | 162 MPa | 23500 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
| Flexural Modulus | 9.45 GPa | 1370 ksi | ASTM D790 |
| Compressive Strength | 165 MPa | 24000 psi | ASTM D695 |
| Izod Impact, Notched | 0.961 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 43.2 µm/m-°C @Temperature 20.0 °C |
24.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
Users viewing this material also viewed the following:
- ICO Polymers ICOTEXâ„¢ 520-5004 1000 Micron EVA Powder
- Haynes 625 alloy, cold rolled and 1050°C mill-annealed sheet
- Spartech Royalite R6000 FR-PC Aircraft Grade Sheet
- Samsung Cheil Industries Infino® PCA-NH1015V Flame Retardant
- Chase Plastics CP Pryme® NN100HSL (COND, 50% RH) Nylon 66, Heat Stabilized, Internally Lubricated
- Chengdu Polyster 6502 High Performance Grade TPV
- Dow AMPLIFY™ GR 205 Maleic anhydride grafted (MAH) polymer
- BASF Ultramid® 8233G HS BK-102 33% Glass Filled PA6 (Conditioned)
- BASF Ultramid® A3HG3 PA66 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved