Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 5.60 GPa | 812 ksi | ISO 178 |
Polyplastic Armlen® PP GF 30-5HS-901 Polypropylene, 30% Glass Filled Heat stabilized, black colorInformation provided by PolyPlastic Group. |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | ISO 178 |
Nilit FRIANYL A63 GV15 Nylon 6.6 for injection molding, 15% glass fiber reinforced Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | ISO 178 |
Nilit FRIANYL A63 W-GV15 Nylon 6.6 for injection molding, 15% glass fiber reinforced Nylon 6.6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | ISO 178 |
Nilit FRIANYL B63 CV10 Nylon 6.6 for injection molding, 10% carbon fiber reinforced Nylon 6.6 for injection molding, good conductive and electrostatic properties.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | |
Plastcom SLOVALEN PH 66 GF 30 FRO 4 PP, 30% glass fibre, mod. of mech. prop. Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.0.. |
|||
Flexural Modulus | 5.60 GPa @Temperature 23.0 °C |
812 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PPH GF3030 PD2 PP, Glass Fiber-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
Flexural Modulus | 5.60 GPa @Temperature 23.0 °C |
812 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PPH GF4030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
Flexural Modulus | 5.60 GPa @Temperature 23.0 °C |
812 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PPH GF5030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | conditioned, 2 mm/min; ISO 178-A |
Lanxess Durethan® AKV 30 G HR DUS023 900116 Nylon 66, 30% Glass Fiber PA 66, 30% glass fiber, injection molding, improved flowability, hydrolysis stabilized, improved surface finish, GIT/WITInformation provided by LANXESS. |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | ISO 178 |
Lanxess Durethan® BKV 15 H3.0 000000 Nylon 6 Copolymer, 15% Glass Fibers PA 6 Copolymer, 15% glass fibers, injection molding, heat-ageing stabilized |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | 2 mm/min; ISO 178-A |
Lanxess Pocan® B 3216 HR 000000 PBT 16% Glass Fiber PBT, 16% glass fibers, injection molding, improved impact strength, hydrolysis stabilizedInformation provided by LANXESS. |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | 2mm/min; ASTM D790 |
Kingfa PBT-RG151 Flame Retardant, 15% Glass Fiber Reinforced PBT Features:Flame retardantHigh strengthHigh temperature propertiesGood electric propertiesExcellent size stabilityNo bloomingApplications:Injection moldingConnectorsRelayBobbinsPlugsE & E partsInforma.. |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Lubricomp KFL34 Acetal Copolymer (Europe-Africa-Middle East) LNP* Lubricomp* KFL34 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® EH7025AG PBT+PET Valox EH7025AG is a mineral filled PBT/PET that offers good surface appearance, good flow and good heat performance. EH7025AG was developed for automotiove bezel application. |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® EH7025AG PBT+PET (Europe-Africa-Middle East) Valox EH7025AG is a mineral filled PBT/PET that offers good surface appearance, good flow and good heat performance. EH7025AG was developed for automotiove bezel application. |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® SHF4340 PBT (Europe-Africa-Middle East) 20% GF Super High Flow PBT |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP MF004AS PP LNP THERMOCOMP* MF004AS is a compound based on Polypropylene resin containing 20% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | ASTM D790 |
Saint-Gobain Meldin® 5001 Thermoplastic Bearing Material General Notes on Meldin 3000/5000 Series Bearing Products:Injection Moldable, High-Performance Bearings. Can withstand environments of high temperature, corrosive, and water.Specific Notes on Meldin.. |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | ASTM D790 |
Tipco Tipcolene® FPTC 60 - 60% Talc & Calcium Carbonate Reinforced Polypropylene Homopolymer Masterbatch 60% Talc+Calcium Reinforced PP HomopolymerApplications: Furniture & AppliancesProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | ISO 178 |
Polyram RamTough PZ324G4NT Polycarbonate, 20% Glass Fiber, Flame Retardant 20% glass fiber reinforced, flame retardant polycarbonate for injection molding applications.Information provided by Polyram. |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | cond; ISO 178 |
DSM Novamid® 1010GH30 NAT PA6-GF30 30% Glass Reinforced, Heat Stabilized, Injection Molding |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | cond; ISO 178 |
DSM Novamid® 1013G30 1 NA PA6-GF30 30% Glass Reinforced, Injection Molding |
|||
Flexural Modulus | 5.60 GPa @Temperature 180 °C |
812 ksi @Temperature 356 °F |
ISO 178 |
DSM Stanyl® OCD2300 BLK PA46-GF50 50% Glass Reinforced, Heat Stabilized |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | 50%RH; ISO 178 |
DuPont Performance Polymers Zytel® 84G33 BKB031 Nylon 66 + Nylon 6
(Unverified Data**) 33% Glass Reinforced Toughened Polyamide 66 + Polyamide 6 Zytel 84G33 BKB031 is a 33% glass reinforced toughened polyamide 66 and polyamide 6 co-melt black cube blended resin. This resin was develop.. |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | 2 mm/min; ISO 178 |
Eurostar Starflam PX08029 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded Starflam PX08029 is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | ASTM D790 |
E-Polymers TEKAMID® TA250G15 , 15% Glass Fiber Reinforced PA66, DAM 15% Glass Fiber Reinforced, Good surfaceInformation provided by E-Polymers Co. Ltd. |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | ISO 178 |
BASF Ultramid® S3EG6 Balance 30% Glass Filled PA 610 (Conditioned) Description: BASF supplies polyamide 610 for processing by injection molding under the trade name Ultramid® Balance which is produced by polycondensation of hexamethylene diamine and sebacic acid. .. |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | ISO 178 |
BASF Ultramid® S3WG6 Balance 30% Glass Filled PA 610 (Conditioned) Description: BASF supplies polyamide 610 for processing by injection molding under the trade name Ultramid® Balance which is produced by polycondensation of hexamethylene diamine and sebacic acid. .. |
|||
Flexural Modulus | 5.60 GPa | 812 ksi | ASTM D790 |
A. Schulman ComAlloy Hiloy® 109 Polypropylene, Glass/Mineral Reinforced, Chemically Coupled Data provided by the manufacturer, ComAlloy International Company.40% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |