SABIC Innovative Plastics LNP Lubricomp KFL34 Acetal Copolymer (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer + Glass/PTFE
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp KFL34 Acetal Copolymer (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* KFL34 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.63 g/cc
0.0589 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
on tensile bar; SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 97.0 MPa
14100 psi
5 mm/min; ISO 527
Elongation at Break 2.5 %
2.5 %
5 mm/min; ISO 527
Tensile Modulus 5.90 GPa
856 ksi
1 mm/min; ISO 527
Flexural Strength 119 MPa
17300 psi
2 mm/min; ISO 178
Flexural Modulus 5.60 GPa
812 ksi
2 mm/min; ISO 178
Izod Impact, Unnotched (ISO) 20.0 kJ/m²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 52.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 28.9 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 112 µm/m-°C

@Temperature 23.0 - 60.0 °C
 62.2 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 160 °C
320 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af