- Polyram RamTough PZ324G4NT Polycarbonate, 20% Glass Fiber, Flame Retardant
Polyram RamTough PZ324G4NT Polycarbonate, 20% Glass Fiber, Flame Retardant
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTough PZ324G4NT Polycarbonate, 20% Glass Fiber, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% glass fiber reinforced, flame retardant polycarbonate for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ISO 2577 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527 |
| Elongation at Break | 2.7 % | 2.7 % | ISO 527 |
| Tensile Modulus | 6.00 GPa | 870 ksi | ISO 527 |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 5.60 GPa | 812 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ISO 75 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
Users viewing this material also viewed the following:
- MV Labs AS850 (NH4)3AsO4 Ammonium arsenate tribasic
- Plastcom SLOVALEN PQ 91 N Polypropylene Homopolymer, Modified with Elastomer, Impacted
- Arkema Group Oroglas® DRM Acrylic, Extrusion Grade (discontinued **)
- Teknor Apex APEX® 65014 Polyvinyl Chloride, Flexible
- A. Schulman PP 1632-01 Polypropylene Random Copolymer
- Dow Corning FOX® PMCP22 Flowable Oxide
- Bhansali Engineering Abstron IMC-45 FR V2 Flame Retardant PC/ABS Grade
- Ascend Performance Materials Vydyne® R533 Nylon 66, 33% Glass Filled, Conditioned (2.5% Moisture)
- DuPont Elvax® 3175LG Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion (discontinued **)
- BNZ Materials Bazelite 2500 LI Insulating Castable
Copyright © lookpolymers.com All Rights Reserved