SABIC Innovative Plastics Valox® EH7025AG PBT+PET (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PET + PBT Unreinforced , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® EH7025AG PBT+PET (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Valox EH7025AG is a mineral filled PBT/PET that offers good surface appearance, good flow and good heat performance. EH7025AG was developed for automotiove bezel application.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.10 % | 0.10 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0080 - 0.0090 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 40 g/10 min @Load 2.16 kg, Temperature 265 °C |
40 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| Melt Index of Compound | 34 g/10 min @Load 2.16 kg, Temperature 265 °C |
34 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 5 mm/min; ISO 527 |
| 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 5.35 GPa | 776 ksi | 1 mm/min; ISO 527 |
| 5.50 GPa | 798 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
| 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 5.10 GPa | 740 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 5.60 GPa | 812 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.310 J/cm | 0.581 ft-lb/in | ASTM D256 |
| 0.300 J/cm @Temperature -30.0 °C |
0.562 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| 2.00 kJ/m² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.100 J/cm² | 0.476 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 46.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 49.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 59.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 62.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C @Thickness 3.20 mm |
374 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 175 °C | 347 °F | Rate B/50; ASTM D1525 |
| 175 °C | 347 °F | Rate B/50; ISO 306 | |
| 177 °C | 351 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- NOVA Chemicals Surpass® IFs932-R Octene SLLDPE Injection Molding Resin
- DSM Akulon® S223-G8U (Dry) 43% Glass Reinforced Nylon 66 (North America) (discontinued **)
- Lehmann & Voss LUVOCOM® 1100-8049 Polyether sulfone, with glass fiber
- Techmer ES Plaslube® NY-1/TF/20 NAT PA66
- DuPont Bynel® 1124 Modified EVA Adhesive Resin
- Loctite® 4081 Cyanoacrylate Adhesive
- Daikin POLYFLON M-111 PTFE Molding Powder, Fine Cut
- Arkema Group Rilsan® BMV 400 TL Nylon 11 (Conditioned)
- A. Schulman POLYBATCH™ Light Grey 80426U Concentrate Based In LLDPE
- Lehmann & Voss LUVOCOM® 1301-8305 PPS, linear, with glass fiber, lubricant modified
Copyright © lookpolymers.com All Rights Reserved