Lanxess Durethan® AKV 30 G HR DUS023 900116 Nylon 66, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Heat Stabilized |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® AKV 30 G HR DUS023 900116 Nylon 66, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, 30% glass fiber, injection molding, improved flowability, hydrolysis stabilized, improved surface finish, GIT/WITInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.343 g/cc | 0.04852 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0064 cm/cm | 0.0064 in/in | 60x60x2; 290°C / MT 80°C; 600 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0082 cm/cm | 0.0082 in/in | 60x60x2; 290°C / MT 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | conditioned, 5 mm/min; ISO 527-1,-2 |
| 135 MPa | 19600 psi | 5 mm/min; ISO 527-1,-2 | |
| Elongation at Break | 3.2 % | 3.2 % | 5 mm/min; ISO 527-1,-2 |
| 6.5 % | 6.5 % | conditioned, 5 mm/min; ISO 527-1,-2 | |
| Tensile Modulus | 5.60 GPa | 812 ksi | conditioned, 1 mm/min; ISO 527-1,-2 |
| 8.50 GPa | 1230 ksi | 1 mm/min; ISO 527-1,-2 | |
| Flexural Strength | 150 MPa | 21800 psi | conditioned, 2 mm/min; ISO 178-A |
| 215 MPa | 31200 psi | 2 mm/min; ISO 178-A | |
| Flexural Modulus | 5.60 GPa | 812 ksi | conditioned, 2 mm/min; ISO 178-A |
| 8.00 GPa | 1160 ksi | 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
conditioned; ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
conditioned; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1U |
| 60.0 kJ/m² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U | |
| 60.0 kJ/m² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
conditioned; ISO 180-1U | |
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
conditioned; ISO 179-1eU | |
| 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
conditioned; ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
conditioned; ISO 179-1eA | |
| Puncture Energy | 2.00 J @Temperature -30.0 °C |
1.48 ft-lb @Temperature -22.0 °F |
ISO 6603-2 |
| 2.50 J @Temperature 23.0 °C |
1.84 ft-lb @Temperature 73.4 °F |
ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
16.7 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Melting Point | 259 °C | 498 °F | 10 °C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1,-2 |
| Deflection Temperature at 8.0 MPa | 75.0 °C | 167 °F | ISO 75-1,-2 |
| Shrinkage | 0.0400 % @Temperature 120 °C, Time 14400 sec |
0.0400 % @Temperature 248 °F, Time 4.00 hour |
post-shrinkage, 60x60x2; ISO 294-4 |
| 0.0500 % @Temperature 120 °C, Time 14400 sec |
0.0500 % @Temperature 248 °F, Time 4.00 hour |
post-shrinkage, transverse, 60x60x2; ISO 294-4 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 °C | 554 °F | Injection molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection molding; ISO 294 |
| Dry Time | 2.00 - 6.00 hour @Temperature 80.0 °C |
2.00 - 6.00 hour @Temperature 176 °F |
|
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer test |
Users viewing this material also viewed the following:
- Palm Labs Adhesives Turbo Anti-Seize Copper Paste
- Momentive Performance Materials "PG" Pyrolytic Graphite
- MetalTek MTEK 625 Cast UNS N26625 Severe Corrosion and Heat Resistant Alloy
- Styrolution Clearblend 145 MBS
- SABIC Innovative Plastics NORYL 731S PPE+PS (Asia Pacific)
- Terio Corporation TZY-4 Yttria Stabilized Zirconia
- TIMET TIMETAL® 5111 Titanium Alloy (Ti-5Al-1Sn-1Zr-1V-0.8Mo; ASTM Grade 32)
- Dow Corning 6-3570 Polymer
- Asia International Enterprise (Hong Kong) 60G6 Nylon 66, 30% Filled
Copyright © lookpolymers.com All Rights Reserved