SABIC Innovative Plastics LNP THERMOCOMP MF004AS PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MF004AS PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* MF004AS is a compound based on Polypropylene resin containing 20% Glass Fiber. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| 1.034 g/cc | 0.03736 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.0300 % | 0.0300 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Time 86400 sec |
0.0040 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0072 cm/cm @Time 86400 sec |
0.0072 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.010 cm/cm @Time 86400 sec |
0.0090 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0095 cm/cm @Time 86400 sec |
0.0095 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
| 65.0 MPa | 9430 psi | ISO 527 | |
| Elongation at Break | 2.2 % | 2.2 % | ISO 527 |
| 2.3 % | 2.3 % | ASTM D638 | |
| Tensile Modulus | 4.55 GPa | 660 ksi | 50 mm/min; ASTM D638 |
| 5.10 GPa | 740 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 92.0 MPa | 13300 psi | ASTM D790 |
| 104 MPa | 15100 psi | ISO 178 | |
| Flexural Modulus | 4.34 GPa | 629 ksi | ASTM D790 |
| 5.60 GPa | 812 ksi | ISO 178 | |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.25 J/cm | 6.09 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Transverse to Flow | 74.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 74.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C @Thickness 3.20 mm |
320 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 149 °C @Thickness 3.20 mm |
300 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Nye Lubricants 781D (NG) Synthetic Oil
- DuPont Nucrel® 30707SR Ethylene-Acrylic Acid Copolymer Resin for Film and Extrusion Coating (discontinued **)
- Schott N-SF66 Glass
- Teknor Apex APEX® 3301-55 Polyvinyl Chloride, Flexible
- Chase Plastics CP Pryme® N300STL (DAM) Nylon 6 (Utility Grade), Super Toughened, Internally Lubricated
- Zylog Hipolyene® GM BP 11 Thermoplastic Polyolefin & PP Compound
- UBE UBESTA® 3030U Nylon 12 (After Fuel C for 500 hours)
- ChevronTexaco Canopus® 46
- Chosun Refractories A-1 Insulating Firebrick
- Eurostar Star L PA66 30V D31 PA66, Glass Fiber Filled, Injection Molded
Copyright © lookpolymers.com All Rights Reserved