SABIC Innovative Plastics Valox® SHF4340 PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® SHF4340 PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% GF Super High Flow PBT
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 |
| Filler Content | 20 % | 20 % | ASTM D229 |
| Moisture Absorption | 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.15 % | 0.15 % | ISO 62 |
| Viscosity | 55000 cP | 55000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
| 95000 cP | 95000 cP | Melt Viscosity, 250°C, 1500 sec-1; ISO 11443 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | on Tensile Bar; SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.010 cm/cm | 0.0040 - 0.010 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 40 g/10 min @Load 2.16 kg, Temperature 250 °C |
40 g/10 min @Load 4.76 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ISO 2039-2 |
| Hardness, H358/30 | 185 MPa | 26800 psi | ISO 2039-1 |
| Tensile Strength at Break | 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D638 |
| 110 MPa | 16000 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D638 |
| 110 MPa | 16000 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| 3.0 % | 3.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 6.70 GPa | 972 ksi | 1 mm/min; ISO 527 |
| 6.80 GPa | 986 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.60 GPa | 812 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| 0.800 J/cm @Temperature 0.000 °C |
1.50 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| 0.800 J/cm @Temperature -30.0 °C |
1.50 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 3.50 J/cm | 6.56 ft-lb/in | ASTM D4812 |
| 3.30 J/cm @Temperature -30.0 °C |
6.18 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature 0.000 °C |
3.81 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/2C |
| 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179/2C | |
| 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
22.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature -40.0 - 40.0 °C |
55.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 223 °C @Thickness 3.20 mm |
433 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 200 °C | 392 °F | Rate B/120; ISO 306 |
| 205 °C | 401 °F | Rate B/50; ISO 306 | |
| 205 °C | 401 °F | Rate B/50; ASTM D1525 | |
| 220 °C | 428 °F | Rate A/50; ISO 306 | |
| 220 °C | 428 °F | Rate A/50; ASTM D1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 18.6 kV/mm @Thickness 3.20 mm |
472 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 25.3 kV/mm @Thickness 1.60 mm |
643 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 33.0 kV/mm @Thickness 0.800 mm |
838 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0182 @Frequency 1.00e+6 Hz |
0.0182 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 375 V | 375 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Advanced Elastomer Systems Santoprene® 451-87 Thermoplastic Rubber (discontinued **)
- 5187 Polyurethane-based Biomedical Elastomer
- Eastman PG400 PET (discontinued **)
- Nilit FRIANYL B63 GV50 Nylon 6 for injection molding, 50% glass fiber reinforced
- Indium Corp. Germanium Corporation® GeCl4 Germanium Tetrachloride
- SABIC Innovative Plastics LNP THERMOCOMP RF008XXH PA 66
- DSM Akulon® K224-HGM35 (Cond.) 15% Glass Reinforced, 25% Mineral Reinforced, Heat Stabilized Nylon 6 (North America)
- BASF Styropor® P 426 Expandable Polystyrene
- Solvay Specialty Polymers Algoflon® F5 PTFE (Polytetrafluoroethylene) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved