Saint-Gobain Meldin® 5001 Thermoplastic Bearing Material
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | Saint-Gobain Perfomance Plastics |
| Trade Name | Meldin® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Saint-Gobain Meldin® 5001 Thermoplastic Bearing Material.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General Notes on Meldin 3000/5000 Series Bearing Products:Injection Moldable, High-Performance Bearings. Can withstand environments of high temperature, corrosive, and water.Specific Notes on Meldin®5001 BearingMeldin® 5001 components offer superior strength in structural applications where electrical insulation combined with intricate part design is required. The melt characteristics of Meldin® 5001 material allow for fine detail, regardless of part complexity.Applications include: Appliances, Automotive, Document Processing Equipment, Industrial, Medical, Transportation.Information provided by Saint Gobain Performance Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Water Absorption | 0.23 % | 0.23 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Yield | 2.8 % | 2.8 % | ASTM D638 |
| Tensile Modulus | 4.80 GPa | 696 ksi | ASTM D 638 |
| Flexural Strength | 169 MPa | 24500 psi | ASTM D790 |
| Flexural Modulus | 5.60 GPa | 812 ksi | ASTM D790 |
| Compressive Strength | 207 MPa | 30000 psi | ASTM D695 |
| Compressive Modulus | 2.90 GPa | 421 ksi | ASTM D695 |
| Poissons Ratio | 0.36 | 0.36 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 34.0 µm/m-°C @Temperature 24.0 - 149 °C |
18.9 µin/in-°F @Temperature 75.2 - 300 °F |
ASTM E831-93 |
| 71.0 µm/m-°C @Temperature 199 - 299 °C |
39.4 µin/in-°F @Temperature 390 - 570 °F |
ASTM E831-93 | |
| Maximum Service Temperature, Air | 316 °C | 600 °F | UL-746 B |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.4 @Frequency 1000 Hz |
3.4 @Frequency 1000 Hz |
ASTM D150 |
| 3.4 @Frequency 10000 Hz |
3.4 @Frequency 10000 Hz |
ASTM D150 | |
| Dielectric Strength | 17.0 kV/mm | 433 kV/in | ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 10000 Hz |
0.0010 @Frequency 10000 Hz |
ASTM D150 |
| Arc Resistance | 135 sec | 135 sec | ASTM D495 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Hardness, Rockwell K | 50 | ASTM D785 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CM6240 PC+ABS (Asia Pacific)
- Polykemi AB POLYshine PBT D211 PBT, Modified
- Greene Tweed CHEMRAZ® 550 Perfluoroelastomer
- A. Schulman POLYBATCH™ Blue 4012 Concentrate Based in Polyethylene
- Zhejiang Juner 302-G0 Flammable Resistant and Low Separate Out Mode
- Beijing Evergrow Resources ASHRAE HEPA ULPA-K69 Glass Fiber Paper
- SABIC Innovative Plastics NORYL GTX CRN730V PPE+PA6 (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved