SABIC Innovative Plastics Lexan® FXM1414T PC Copolymer

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FXM1414T PC Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC-siloxane copolymer in special metallic colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Moisture Absorption 0.0900 %
0.0900 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.12 %
0.12 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
on Tensile Bar; SABIC Method
0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 9.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
9.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 47.0 MPa
6820 psi
50 mm/min; ISO 527
48.0 MPa
6960 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 56.0 MPa
8120 psi
50 mm/min; ISO 527
58.0 MPa
8410 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 78 %
78 %
Type I, 50 mm/min; ASTM D638
89 %
89 %
50 mm/min; ISO 527
Elongation at Yield 5.4 %
5.4 %
50 mm/min; ISO 527
5.7 %
5.7 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.26 GPa
328 ksi
50 mm/min; ASTM D638
2.27 GPa
329 ksi
1 mm/min; ISO 527
Flexural Yield Strength 85.0 MPa
12300 psi
1.3 mm/min, 50 mm span; ASTM D790
88.0 MPa
12800 psi
2 mm/min; ISO 178
Flexural Modulus 2.12 GPa
307 ksi
2 mm/min; ISO 178
2.23 GPa
323 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 5.20 J/cm
9.74 ft-lb/in
ASTM D256
2.70 J/cm

@Temperature -30.0 °C
5.06 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 30.0 kJ/m²
14.3 ft-lb/in²
80*10*4; ISO 180/1A
14.0 kJ/m²

@Temperature -30.0 °C
6.66 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 4.00 J/cm²
19.0 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 57.0 J

@Temperature 23.0 °C
42.0 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 67.5 µm/m-°C

@Temperature -40.0 - 95.0 °C
37.5 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
67.5 µm/m-°C

@Temperature 23.0 - 80.0 °C
37.5 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 95.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
80.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
120 °C

@Thickness 3.20 mm
248 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 138 °C
280 °F
Rate B/50; ISO 306
139 °C
282 °F
Rate B/50; ASTM D1525
142 °C
288 °F
Rate B/120; ISO 306
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASS
IEC 60695-10-2
Copyright © lookpolymers.com All Rights Reserved