SABIC Innovative Plastics LNP THERMOTUF MF0049I PP (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF MF0049I PP (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOTUF* MF0049I is a compound based on Polypropylene resin containing Glass Fiber, Flame Retardant. Added features include; Flame Retardant, Chemically Coupled.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0034 cm/cm | 0.0034 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.7 % | 3.7 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 5.30 GPa | 769 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.70 GPa | 682 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 32.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
17.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 118 µm/m-°C @Temperature 23.0 - 60.0 °C |
65.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Nylene® 452 Nylon 6
- Precision Polymer Engineering Q90Y Polyurethane Rubber
- H.C. Starck Amperit® 720.054 Blended Chromium Oxide-Aluminum Oxide-Titanium Oxide 80-17-3 (Cr2O3-Al2O3-TiO2)
- Karina E 844-10/176-CRB White PVC Compound
- Loctite® 3106 Acrylic Light Cure Adhesive
- DSM Akulon® S223-D Nylon 66 (European Grade) (Cond)
- Barlog Plastics KEBAFORM C 6027 POM Copolymer, 30% mineral reinforced
- Covestro Makrofol® LT 4-4 Polycarbonate
- KKPC KOSYN SOL 5520 Solution Styrene Butadiene Rubber (S-SBR)
Copyright © lookpolymers.com All Rights Reserved