SABIC Innovative Plastics Lexan® EXL1464T PC Copolymer (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® EXL1464T PC Copolymer (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lexan* EXL1464T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers extreme low temperature (-40 °C) ductility in combination with medium flow characteristics, improved release and excellent processability with opportunities for shorter IM cycle times compared to standard PC. Lexan EXL1464T resin is an improved release general purpose product available in transparent and opaque colors and is an excellent candidate for a broad range of applications.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D 792
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.090 %
0.090 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.12 %

@Temperature 23.0 °C
 0.12 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 9.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 9.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Hardness, Rockwell L 87
87
ISO 2039-2
Tensile Strength at Break 55.0 MPa
7980 psi
50 mm/min; ISO 527
59.0 MPa
8560 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 56.0 MPa
8120 psi
50 mm/min; ISO 527
57.0 MPa
8270 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 108.5 %
108.5 %
50 mm/min; ISO 527
123.9 %
123.9 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 5.4 %
5.4 %
50 mm/min; ISO 527
5.6 %
5.6 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.18 GPa
316 ksi
50 mm/min; ASTM D 638
2.30 GPa
334 ksi
1 mm/min; ISO 527
Flexural Yield Strength 88.0 MPa
12800 psi
2 mm/min; ISO 178
92.0 MPa
13300 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.12 GPa
307 ksi
2 mm/min; ISO 178
2.18 GPa
316 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 7.12 J/cm

@Temperature -30.0 °C
 13.3 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
8.24 J/cm

@Temperature 23.0 °C
 15.4 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Notched (ISO) 55.0 kJ/m²

@Temperature -30.0 °C
 26.2 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1A
65.0 kJ/m²

@Temperature 23.0 °C
 30.9 ft-lb/in²

@Temperature 73.4 °F
 80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 80*10*3; ISO 180/1U
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 6.00 J/cm²

@Temperature -30.0 °C
 28.6 ft-lb/in²

@Temperature -22.0 °F
 V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
7.00 J/cm²

@Temperature 23.0 °C
 33.3 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Impact Test 75.0 J

@Temperature 23.0 °C
 55.3 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
77.0 J

@Temperature -30.0 °C
 56.8 ft-lb

@Temperature -22.0 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 67.0 µm/m-°C

@Temperature -40.0 - 95.0 °C
 37.2 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E 831
67.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 37.2 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 95.0 °C
 44.4 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E 831
80.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 44.4 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 116 °C
241 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
120 °C

@Thickness 3.20 mm
 248 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 138 °C
280 °F
Rate A/50; ASTM D 1525
138 °C
280 °F
Rate B/50; ISO 306
139 °C
282 °F
Rate B/120; ISO 306
UL RTI, Electrical 130 °C
266 °F
UL 746B
UL RTI, Mechanical without Impact 130 °C
266 °F
UL 746B
Flammability, UL94 V-2

@Thickness 3.00 mm
 V-2

@Thickness 0.118 in
 UL 94
Glow Wire Test 850 °C

@Thickness 0.800 mm
 1560 °F

@Thickness 0.0315 in
 Glow Wire Ignitability Temperature; IEC 60695-2-13
850 °C

@Thickness 3.00 mm
 1560 °F

@Thickness 0.118 in
 Glow Wire Ignitability Temperature; IEC 60695-2-13
960 °C

@Thickness 3.00 mm
 1760 °F

@Thickness 0.118 in
 Glow Wire Flammability Index; IEC 60695-2-12
Optical Properties Metric English Comments
Haze 3.0 %

@Thickness 2.54 mm
 3.0 %

@Thickness 0.100 in
 ASTM D 1003
Transmission, Visible 82 %

@Thickness 2.54 mm
 82 %

@Thickness 0.100 in
 ASTM D 1003
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ASTM D 257
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ASTM D 257
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C pass
IEC 60695-10-2