SABIC Innovative Plastics Lexan® ADX1016R PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® ADX1016R PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lexan Copolymer resin with improved chemical resistance, available only in limited colors.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.40 % | 0.40 % | ISO 62 |
| Melt Index of Compound | 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 73.0 MPa | 10600 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 79 % | 79 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 7.0 % | 7.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.29 GPa | 332 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.25 GPa | 326 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 51.0 kJ/m² | 24.3 ft-lb/in² | 80*10*3; ISO 180/1A |
| 23.0 kJ/m² @Temperature -30.0 °C |
10.9 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 5.00 J/cm² | 23.8 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 2.40 J/cm² @Temperature -30.0 °C |
11.4 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 125 °C | 257 °F | Rate B/50; ISO 306 |
| 126 °C | 259 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 TF-GV 1530 Nylon 6.6 for injection molding, 15% PTFE lubricated and 30% glass fiber reinforced
- PolyOne Geon™ HC 2180 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Glastic Laminates/Shapes 2015 Fiberglass-Reinforced Polyester Standoff Insulator
- Gwent Electronic Materials C2050712D58 Silver Ink for ITO Substrates
- Kareline Oy PPMS5050 Natural Fiber Reinforced Polypropylene for injection molding
- Silberline Sparkle Silvex® Premier 950-20-D
- DSM Akulon® S227-C Nylon 66 (European Grade) (Dry)
- COI Ceramics SiC Hollow Spheres
- Beijing Ranger Chem 164 Liquid Epoxy Resin
- Axiall 19912 Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved