SABIC Innovative Plastics LNP STAT-KON RX06001 PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON RX06001 PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* RX06001 is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include: Easy Molding, High Impact, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | on Tensile Bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 135 MPa | 19600 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 82.0 MPa | 11900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.5 % | 3.5 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 8.30 GPa | 1200 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 173 MPa | 25100 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 182 MPa | 26400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.00 GPa | 870 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
12.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 109 µm/m-°C @Temperature 23.0 - 60.0 °C |
60.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 249 °C | 480 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10000 ohm - 1e+05 | 10000 ohm - 1e+05 | ASTM D257 |
Users viewing this material also viewed the following:
- Osprey Metals M2/MA Tool Steel Master Alloy Powder (Grade 90% - 22)
- Quadrant EPP Quadrant PPSU LSG PPSU, Extruded, Unfilled, Polyphenylsulfone (ASTM Product Data Sheet)
- Glastic Laminates/Shapes 1872 Fiberglass-Reinforced Polyester Standoff Insulator
- Lord Adhesives Thermosetâ„¢ SC-102 Unfilled Silicone Encapsulant
- Borealis Daplen™ EE189AI Polypropylene TPO Compound
- Clariant Renol TES3050A Thermoplastic Elastomer Alloy
- DuPont Performance Polymers Zytel® 73G30T NC010 Nylon 6 (Unverified Data**)
- Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) + Aged 1200°F (650°C)
Copyright © lookpolymers.com All Rights Reserved