SABIC Innovative Plastics LNP LUBRILOY RX05497 PA 66 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Lubriloy
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRILOY RX05497 PA 66 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRILOY* RX05497 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
ASTM D792
1.12 g/cc
0.0405 lb/in³
ISO 1183
Moisture Absorption 0.880 %
0.880 %
50% RH, 24 hrs; ASTM D570
1.18 %
1.18 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.023 - 0.025 cm/cm

@Time 86400 sec
0.023 - 0.025 in/in

@Time 24.0 hour
ASTM D955
0.0231 - 0.0252 cm/cm

@Time 86400 sec
0.0231 - 0.0252 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.023 - 0.025 cm/cm

@Time 86400 sec
0.023 - 0.025 in/in

@Time 24.0 hour
ASTM D955
0.0231 - 0.0252 cm/cm

@Time 86400 sec
0.0231 - 0.0252 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 57.0 MPa
8270 psi
ISO 527
67.0 MPa
9720 psi
ASTM D638
Tensile Strength, Yield 69.0 MPa
10000 psi
ISO 527
82.0 MPa
11900 psi
ASTM D638
Elongation at Break 24.4 %
24.4 %
ASTM D638
31.4 %
31.4 %
ISO 527
Elongation at Yield 5.2 %
5.2 %
ASTM D638
17.2 %
17.2 %
ISO 527
Tensile Modulus 2.73 GPa
396 ksi
1 mm/min; ISO 527
3.04 GPa
441 ksi
50 mm/min; ASTM D638
Flexural Strength 90.0 MPa
13100 psi
ISO 178
105 MPa
15200 psi
ASTM D790
Flexural Modulus 2.43 GPa
352 ksi
ISO 178
2.79 GPa
405 ksi
ASTM D790
Izod Impact, Notched 0.640 J/cm
1.20 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 137 kJ/m²
65.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 60.0 J
44.3 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 76.0 J
56.1 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.30
0.30
ASTM D3702 Modified
Coefficient of Friction, Static 0.16
0.16
ASTM D3702 Modified
K (wear) Factor 20.1 x 10-8 mm³/N-M
10.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 98.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
54.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
98.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
54.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 91.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
50.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
91.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
50.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 58.0 °C
136 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
58.0 °C

@Thickness 3.20 mm
136 °F

@Thickness 0.126 in
unannealed; ASTM D648