SABIC Innovative Plastics LNP THERMOTUF WF006I PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF WF006I PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermotuf* WF006I is a compound based on Polybutylene Terephalate resin containing Glass Fiber. Added features of this material include: High Impact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | on Tensile Bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 101 MPa | 14600 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 82.0 MPa | 11900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.6 % | 3.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 7.60 GPa | 1100 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.00 GPa | 1020 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 26.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
14.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 123 µm/m-°C @Temperature 23.0 - 60.0 °C |
68.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 7% Plasticizer (discontinued **)
- LG Chemical LUPOL HI5205R PP+MF20%, High Impact
- Multibase Multi-Flex® TPE A 5010 BLK
- SABIC Innovative Plastics ULTEM 3452 PEI
- SABIC Innovative Plastics XYLEX X7519HP PC+POLYESTER (Asia Pacific)
- A. Schulman POLYBATCH™ Beige 60199 Concentrate Based In LLDPE
- Epoxy Technology EPO-TEK® P1011S Electrically Conductive Modified Polyimide
- Dow LDPE 641I Low Density Polyethylene, Liner Film Grade
- Solvay Specialty Polymers Amodel® AF-1145 V0 Polyphthalamide (PPA) Resin, 45% Glass Reinforced, at 50% RH (di
- PlastxWorld CEVIAN® B5522 10% GF PBT/ABS Alloy
Copyright © lookpolymers.com All Rights Reserved