SABIC Innovative Plastics LNP THERMOCOMP DF003E PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF003E PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* DF003E is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ASTM D792 |
| 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0054 cm/cm @Time 86400 sec |
0.0054 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0063 cm/cm @Time 86400 sec |
0.0063 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 77.0 MPa | 11200 psi | ASTM D638 |
| 78.0 MPa | 11300 psi | ISO 527 | |
| Tensile Strength, Yield | 82.0 MPa | 11900 psi | ASTM D638 |
| 82.0 MPa | 11900 psi | ISO 527 | |
| Elongation at Break | 4.4 % | 4.4 % | ISO 527 |
| 5.0 % | 5.0 % | ASTM D638 | |
| Elongation at Yield | 3.2 % | 3.2 % | ASTM D638 |
| 3.3 % | 3.3 % | ISO 527 | |
| Tensile Modulus | 4.75 GPa | 689 ksi | 1 mm/min; ISO 527 |
| 4.82 GPa | 699 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
| Flexural Modulus | 4.13 GPa | 599 ksi | ASTM D790 |
| 4.30 GPa | 624 ksi | ISO 178 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.07 J/cm | 17.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 20.0 J | 14.8 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 6.00 J | 4.43 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 68.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 34.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 35.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 144 °C | 291 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 143 °C @Thickness 3.20 mm |
289 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- NCMT NanoPAC™ HS403 High Performance Polypropylene Nanocomposite
- Radici Radilon® CA HS (cond.) Nylon 66/6
- Lehmann & Voss LUVOCOM® 80-7653 Polyacetal-copolymer, with carbon fiber
- Garlock GYLON® HP3563 PTFE Gasketing, Steel Insert, Oxygen Service
- Haynes HR-160® alloy, plate, aged 4000 hours at 760°C (1400°F)
- Shakespeare CL-10XT Super Tough Nylon Copolymer Fishing Line, 8 lb
- Shakespeare Sanstat® CN125 .36mm Nylon 66 Monofilament
- A. Schulman POLYBLAK™ 2723Pm Premium Black Color Concentrate, 25% Carbon Black Based In HDPE
- Arkema Group Rilsan® AZM 30 GT8LD Nylon 12, 30% Glass Fiber Filled (Conditioned)
Copyright © lookpolymers.com All Rights Reserved