SABIC Innovative Plastics LNP STAT-LOY PF303 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY PF303 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-LOY* PF303 is a Nylon 6 base resin containing 15% Glass Fiber. Added features of this grade includes: Antistat.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 | |
| Moisture Absorption | 6.60 % | 6.60 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 68.0 MPa | 9860 psi | 5 mm/min; ISO 527 |
| 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 72.0 MPa | 10400 psi | 5 mm/min; ISO 527 |
| 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D638 |
| 2.8 % | 2.8 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 |
| 2.3 % | 2.3 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.74 GPa | 687 ksi | 1 mm/min; ISO 527 |
| 5.62 GPa | 815 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 103 MPa | 14900 psi | ISO 178 |
| 120 MPa | 17400 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 121 MPa | 17500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.25 GPa | 616 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.25 GPa | 616 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.930 J/cm | 1.74 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.49 J/cm | 14.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 44.0 kJ/m² | 20.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 31.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
17.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 137 µm/m-°C @Temperature -30.0 - 30.0 °C |
76.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C | 399 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 207 °C @Thickness 3.20 mm |
405 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 181 °C | 358 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 188 °C @Thickness 3.20 mm |
370 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 9.0 - 11 ohm | 9.0 - 11 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Radici Radilon® S ESL128 (dry) Nylon 6
- SABIC Innovative Plastics Lexan® FXM4701 PPC
- Abatron 4823 A/B Filled Potting Compound (discontinued **)
- Saint-Gobain Chemfab® TCK® 1589 High-Strength Plain Weave Open Mesh Belting Material
- Trelleborg B937 Nitrile Rubber
- Trelleborg Sealing Solutions HiMod® 914 Thermoplastic Bearing
- Crucible Steel 303 SE Chromium-Nickel Steel
- Clariant Renol PURSP0005 Polyurethane Elastomer, Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved