- Polymer Property : Tensile Strength, Yield = 34.0 MPa
Polymer Property : Tensile Strength, Yield = 34.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 4.0 mm thick, 10.0 mm wide molded rod; ISO 527 |
| Premix Thermoplastics PRE-ELEC® ESD 7120 PRE-ELEC ESD 7120 is a static dissipative thermoplastic compound based on ABS. The dissipative property is permanent and built into the polymer chain. PRE-ELEC ESD 7120 has been developed for inject.. |
|||
| Tensile Strength, Yield | 34.0 - 55.0 MPa | 4930 - 7980 psi | Average value: 43.7 MPa Grade Count:49 |
| Overview of materials for Polystyrene, Transparent Grade This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Transparent Grade". Each property range of values reported is minimum and maximum values of.. |
|||
| Tensile Strength, Yield | >= 34.0 MPa | >= 4930 psi | ASTM D638 |
| NIZHNEKAMSKNEFTEKHIM PP 1510M (X30S) Propylene Homopolymer Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P.. |
|||
| Tensile Strength, Yield | >= 34.0 MPa | >= 4930 psi | ASTM D638 |
| NIZHNEKAMSKNEFTEKHIM PP 1552N (YF39S) Propylene Homopolymer Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P.. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 50mm/min; ASTM D638 |
| Reliance Industries Repol H200FG Polypropylene REPOL Polypropylene H200FG is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific cataly.. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Ineos H38G-01 Polypropylene Homopolymer, Fiber Grade
(discontinued **) Suggested fabrication methods: Fiber spinningFeatures: Very high speed spinning, Low gas fadeTypical applications: Spunbound fabricsComplies with FDA specification, Title 21, CFR 177.1520.Typical pr.. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Flint Hills P4C4T-189 Polypropylene Homopolymer Features: Visbroken, Antistat. Product does not contain animal derived components. Phthalate-free.Applications: Injection Molding: ClosuresInformation Provided by Flint Hills Resources |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Flint Hills P4C5T-013 Homopolymer Polypropylene Homopolymer, UL certified, and FDA compliant.Features: Antistat, and controlled rheology.Applications: Injection molding: general purpose.Former Huntsman polypropylene products are now produced by F.. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| LG Chemical LUMAX HF-5006F High Flow PBT, Weather Resistant, Flame Retardant LUMAX resins are a family of thermoplastic blends of polybutyleneterephthalate(PBT) and styrenic resins that combine the most desirable properties of both resins and fillers. They offer high heat r.. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Global PP-1100-RC Polypropylene Homopolymer Description-transparency, high stiffness, high heat resistantApplications-general purpose, household goodsInformation provided by Global Polymers Corporation. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP DZL34E PC LNP* Lubricomp* DZL34E is a compound based on Polycarbonate resin containing 20% Milled Glass, 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP ML003S PP LNP* LUBRICOMP* ML003S is a compound based on Polypropylene resin containing 15% PTFE. Added features include: Heat Stabilized, Wear Resistant. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-LOY 63000CT PC+POLYESTER (Asia Pacific) A permanent antistatic PC-Alloy compound that features transparency and superior cleanliness for advanced semiconductor packaging applications |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 50mm/min; ISO 527 |
| Styrolution Terblend® N NM-11 ABS/PA6 (Conditioned) Terblend N NM-11 is an ABS/PA6 blend combining very high impact strength, even at low temperatures, with an excellent processability and surface appearance.Information provided by STYROLUTION, which.. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ISO 527-1/-2 |
| Styrolution Terblend® N NM-19 XP Beige 38163 ABS+PA (Conditioned) Description: Terblend® N NM-19 XP is an UV stabilized ABS/PA blend combining very high impact strength, even at low temperatures with an outstanding processability and excellent surface appearanc.. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL PPX PPX7200 PPE+PP+PS (Asia Pacific) PP+PPE+PS. Improved chemical resistance and surface aesthetics in injection molded applications. NSF61-capable. UL-94 HB listed. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 50mm/min; ISO 527-2 |
| Borealis BH980MO Polypropylene Copolymer BH980MO is a heterophasic copolymer. This grade provides very high stiffness, high gloss and low stress whitening. and is designed for high-speed injection molding and contains nucleating and antist.. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| A. Schulman POLYFORT™ FPP 1310 Coupled Mica Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1310 is a Coupled Mica filled homopolymer polypropylene compound for injection molding.Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ISO 527-2 |
| Total PPH 11012 Polypropylene Homopolymer, Injection Molding Polypropylene PPH 11012 is a nucleated controlled-rheology antistatic homopolymer with a high melt flow index of 55 g/10 min.Polypropylene PPH 11012 is characterized by high fluidity for high speed .. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| A. Schulman POLYFORT™ FPP1666 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1666 is a 10% talc filled homopolymer polypropylene compound. Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | dry; ISO 527-1/-2 |
| EMS-Grivory Grivory® R 47 HW 10 PA6 Grilon R 47 HW 10 is a flexible, cold impact resistant and heat stabilized polyamide 6 for applications in the extrusion. The material can be processed on all for polyamides suitable tube-extrusion .. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Entec Hypro™ PPH-T20 Homopolymer Polypropylene, 20% Talc Reinforced Information provided by Entec |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Aclo Accutech Polypropylene Homopolymer HP0334M20L Mica Reinforced |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | |
| BASF Polystyrol® 456 F Impact Grade Polystyrene (Europe) Heat distortion resistant, good flowing grade for parts subjected to heat.Data was collected by ISO methods and provided by BASF. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Braskem H 103 Extrusion Coating Polypropylene Homopolymer Description: H 103 is a high melt flow rate additivated homopolymer used for general purposes. The product exhibits excellent processing performance on injection moulding applications. Applications:.. |
|||
| Tensile Strength, Yield | 34.0 - 40.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
4930 - 5800 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Solvay Specialty Polymers Solef® 60512 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 60512 PVDF copolymer has high viscosity of the melt and it is a grade for offshore piping.Information provided by Solvay Specialty Polymers. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics SABIC PPCOMPOUND 19T1030 PP SABIC® PPcompound 19T1030 is a general purpose, talc filled, heat stabilized homopolymer polypropylene compound. This compound exhibits high flow and is suitable for injection molding applications... |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ISO 527 |
| Unipetrol PP MONSTEN® FC 110 Polypropylene Homopolymer Applications include injection molding, packaging films, and thermoforming. Basic stabilization. Homopolymer.Information provided by Unipetrol RPA |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| BP Amoco Amoco® 6361 Polypropylene Homopolymer
(discontinued **) Suggested fabrication methods: Extrusion; Blow moldingFeatures: Ease of processingTypical applications: Oriented film, Sheet, Fiber, Profile, Consumer productsComplies with FDA specification, Title .. |
|||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Braskem H 510 Bioriented Film Polypropylene Applications: Bioriented films for conversion; adhesive tapes; textile and food packing. Information provided by Braskem |
|||