Styrolution Terblend® N NM-19 XP Beige 38163 ABS+PA (Conditioned)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon |
| Manufacturer | Styrolution |
| Trade Name | Terblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Terblend® N NM-19 XP Beige 38163 ABS+PA (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Terblend® N NM-19 XP is an UV stabilized ABS/PA blend combining very high impact strength, even at low temperatures with an outstanding processability and excellent surface appearance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | 23°C/50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | ISO 2577 |
| Melt Flow | 42.8 g/10 min @Load 10.0 kg, Temperature 240 °C |
42.8 g/10 min @Load 22.0 lb, Temperature 464 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 103 | 103 | ISO 2039-2 |
| Ball Indentation Hardness | 70.0 MPa @Load 36.5 kg, Time 30.0 sec |
10200 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ISO 527-1/-2 |
| Elongation at Break | 35 % | 35 % | Nominal; ISO 527-1/-2 |
| Elongation at Yield | 5.5 % | 5.5 % | ISO 527-1/-2 |
| Tensile Modulus | 1.40 GPa | 203 ksi | ISO 527-1/-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 102 °C | 216 °F | VST/B/50; ISO 306 |
| 160 °C | 320 °F | VST/A/50; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.055 @Frequency 1.00e+6 Hz |
0.055 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Beige 38163 | |
| Commercial Status | Europe | |
| Primary Processing Technique | Injection Molding and Extrusion |
Users viewing this material also viewed the following:
- LG Chemical LUCEL N109LDS POM, Chemical Resistance
- Taiwan Sheen Soon Sheenthane® AH-573 TPU for Hotmelt Adhesive
- SABIC Innovative Plastics LNP Thermocomp 5X06476 FP-V (PVDF)
- SABIC Innovative Plastics LNP THERMOCOMP JF003XXZ PES
- A. Schulman PP 1930L-01 Polypropylene Copolymer Polypropylene
- Daikin POLYFLON MG-1050F PTFE 25% Glass Fiber Filled Molding Powder, High Apparent Density, Free Flow
- Aremco HiE-Coat™ 840-MS High Emissivity Coating, Silicone-Ceramic Filled
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 0.75 PHR Sulfur
Copyright © lookpolymers.com All Rights Reserved