BASF Polystyrol® 456 F Impact Grade Polystyrene (Europe)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | BASF |
| Trade Name | Polystyrol® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Polystyrol® 456 F Impact Grade Polystyrene (Europe).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Heat distortion resistant, good flowing grade for parts subjected to heat.Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.0055 cm/cm | 0.0055 in/in | |
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | |
| Elongation at Break | 30 % | 30 % | |
| Elongation at Yield | 1.8 % | 1.8 % | |
| Tensile Modulus | 2.25 GPa | 326 ksi | |
| Charpy Impact Unnotched | 12.0 J/cm² | 57.1 ft-lb/in² | |
| 9.00 J/cm² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C @Temperature 20.0 °C |
55.6 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | |
| Vicat Softening Point | 94.0 °C | 201 °F | |
| Flammability, UL94 | HB @Thickness 3.05 mm |
HB @Thickness 0.120 in |
|
| Oxygen Index | 18 % | 18 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
|
| 2.5 @Frequency 1e+6 Hz |
2.5 @Frequency 1e+6 Hz |
||
| Dissipation Factor | 0.00015 @Frequency 100 Hz |
0.00015 @Frequency 100 Hz |
|
| 0.00040 @Frequency 1e+6 Hz |
0.00040 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 425 V | 425 V |
Users viewing this material also viewed the following:
- Kennametal Stellite Stellite® 3 PM with P/M Processing
- Monmouth Rubber & Plastics Durafoamâ„¢ C122A Neoprene/SBR
- Solvay Specialty Polymers Amodel® A-1145 DW Polyphthalamide (PPA), 45% Glass Fiber
- Shamrock Technologies Fluoro T® 603 Thermoplastic Grade PTFE Additive
- Wellman Wellamid® NY1599-BK11 Unfilled Nylon 66
- 3M Scotchgard™ 1004MS Multi-Layer Protective Films
- 3M Scotchlite™ 680CR-14 Removable Reflective Graphic Film with Comply™ Adhesive
- BASF Elastollan® C-60D Polyester Type Polyurethane Elastomer
- BASF Ultramid® BU50I PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved