SABIC Innovative Plastics LNP LUBRICOMP ML003S PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP ML003S PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* ML003S is a compound based on Polypropylene resin containing 15% PTFE. Added features include: Heat Stabilized, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.990 g/cc | 0.990 g/cc | ASTM D792 |
| Density | 0.990 g/cc | 0.0358 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 27.0 MPa | 3920 psi | Type I, 5 mm/min; ASTM D638 |
| 28.0 MPa | 4060 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | 5 mm/min; ISO 527 |
| 34.0 MPa | 4930 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 18 % | 18 % | 5 mm/min; ISO 527 |
| 23 % | 23 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 5.0 % | 5.0 % | 5 mm/min; ISO 527 |
| 6.0 % | 6.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.68 GPa | 244 ksi | 1 mm/min; ISO 527 |
| 1.98 GPa | 287 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 42.0 MPa | 6090 psi | ISO 178 |
| Flexural Modulus | 1.59 GPa | 231 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 1.70 GPa | 247 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.380 J/cm | 0.712 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.99 J/cm | 9.35 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J @Temperature 23.0 °C |
2.21 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 91.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
50.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 106 µm/m-°C @Temperature -30.0 - 30.0 °C |
58.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 111 °C @Thickness 3.20 mm |
232 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 57.0 °C @Thickness 3.20 mm |
135 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD/ID/L: 20-40/5-10 nm/1-2 um Short Multi-Walled Carbon Nanotubes
- Industeel SIRIUS 314 25% Cr - 1.8% Si Heat Resistant Stainless Steel
- Styron EMERGEâ„¢ 7100 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS)
- PlastxWorld CEVIAN® A5624 20% GF PA/ABS Alloy, DAM
- PlastxWorld Veroplas PB3301F Nylon 66
- Eastman Tenite Butyrate 285A2R30010 Natural, Trsp Cellulose Acetate Butyrate
- CLAL-MSX NICLAFOR® 1000 TD1 Quenched/Cold Rolled, Rolled Copper Alloy
- Arlon P30670R020 0.020" (0.508 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Solvay Specialty Polymers Solef® 11008 PVDF Copolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved