SABIC Innovative Plastics NORYL PPX PPX7200 PPE+PP+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polypropylene (PP) , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl PPX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PPX PPX7200 PPE+PP+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PP+PPE+PS. Improved chemical resistance and surface aesthetics in injection molded applications. NSF61-capable. UL-94 HB listed.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.990 g/cc | 0.990 g/cc | ASTM D792 |
| Density | 0.990 g/cc | 0.0358 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.050 % | 0.050 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 16 g/10 min @Load 5.00 kg, Temperature 260 °C |
16 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Melt Index of Compound | 18 g/10 min @Load 5.00 kg, Temperature 260 °C |
18 g/10 min @Load 11.0 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 27.0 MPa | 3920 psi | Type I, 50 mm/min; ASTM D638 |
| 28.0 MPa | 4060 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | Type I, 50 mm/min; ASTM D638 |
| 34.0 MPa | 4930 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 115 % | 115 % | 50 mm/min; ISO 527 |
| 130 % | 130 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 8.2 % | 8.2 % | 50 mm/min; ISO 527 |
| 10 % | 10 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 1.24 GPa | 180 ksi | 50 mm/min; ASTM D638 |
| 1.67 GPa | 242 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 48.0 MPa | 6960 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 48.0 MPa | 6960 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 1.44 GPa | 209 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 1.60 GPa | 232 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.49 J/cm | 2.79 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 14.41 J/cm | 27.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 36.0 J @Temperature 23.0 °C |
26.6 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 99.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
55.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 99.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
55.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 108 µm/m-°C @Temperature -40.0 - 40.0 °C |
60.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 108 µm/m-°C @Temperature -40.0 - 40.0 °C |
60.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C @Thickness 3.20 mm |
230 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.0 °C | 163 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 71.0 °C @Thickness 3.20 mm |
160 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 103 °C | 217 °F | Rate B/50; ISO 306 |
| 107 °C | 225 °F | Rate B/120; ISO 306 | |
| 146 °C | 295 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- Radici Radilon® S 35FL (cond.) Nylon 6
- Dielectric Polymers NT-1020 Silicone/Acrylic Double Coated Tape (discontinued **)
- Lucite International Elvacite ® 2046 Acrylic Resin
- Haysite ETR-FR-C Glass Reinforced Polyester Sheet, Electrical Grade (GPO3)
- Hexcel® HexWeb® CR-PAA™ 3/8-5052-0.001 Phosphoric Acid Anodized Aluminum Honeycomb
- Chisso Z CLEAN® E2001 Purging Solution
- Arkema Group Rilsan® AMN P20 TLD Nylon 12, Flexible, Injection Grade (Dry)
- Armstrong C-1/A Epoxy Adhesive
- Fiberfil® J-68/20/E Polypropylene Copolymer, 20% Glass Fiber Reinforced, Chemically coupled
Copyright © lookpolymers.com All Rights Reserved