LG Chemical LUMAX HF-5006F High Flow PBT, Weather Resistant, Flame Retardant
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant |
| Manufacturer | LG Chemical |
| Trade Name | LUMAX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMAX HF-5006F High Flow PBT, Weather Resistant, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LUMAX resins are a family of thermoplastic blends of polybutyleneterephthalate(PBT) and styrenic resins that combine the most desirable properties of both resins and fillers. They offer high heat resistance, impact resistance, and processability requirements of a wide range of applications.Applications: Automotive: Back beam, roof molding, instrument panel, cowl vent grill, speaker frame, lamp parts, glove box housingElectrical and Electronic: Household appliances housings and internal parts, key top, switch, compressor terminal board, cd changer, deck items, floppy disc carriage, electric tool housingIndustrial Parts and Household Appliance: Lawn mower housing, motor housing, pump impellerInformation Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| Flexural Modulus | 1.57 GPa | 228 ksi | ASTM D790 |
| Izod Impact, Notched | 1.30 J/cm @Temperature 23.0 °C |
2.44 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 220 °C | 374 - 428 °F | |
| Middle Barrel Temperature | 220 - 240 °C | 428 - 464 °F | |
| Front Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |
| Nozzle Temperature | 230 - 250 °C | 446 - 482 °F | |
| Melt Temperature | 230 - 250 °C | 446 - 482 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 100 - 120 °C | 212 - 248 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Injection Pressure | 58.84 - 88.26 MPa | 8534 - 12800 psi | Second |
| 63.74 - 93.16 MPa | 9245 - 13510 psi | First | |
| Back Pressure | 1.96 - 4.90 MPa | 284 - 711 psi | |
| Screw Speed | 70 - 100 rpm | 70 - 100 rpm |
Users viewing this material also viewed the following:
- Nylene® 9110 Unfilled Nylon 6/10
- Osprey Metals CE17M Al-Si Controlled Expansion Alloy
- DSM Arnite® D00 301 PET (European Grade) (discontinued **)
- SABIC Innovative Plastics Valox® VX8015U PBT+PET (Europe-Africa-Middle East)
- Tipco Tipcolene® FPT 10 - 10% Talc Reinforced Polypropylene Homopolymer
- Hexcel® HexPly® F593 Epoxy Resin, W3T282 Carbon Fabric
- EMS-Grivory Grivory® XE 4107 black 9992 PA612-GF40
- Fainplast Compounds Hax™ HF 4021/TC Flame Retardant Polyolefin Cable Compound
- BASF Gusspolyamid® Nylon 6 (At 50% RH)
Copyright © lookpolymers.com All Rights Reserved