SABIC Innovative Plastics LNP STAT-LOY 63000CT PC+POLYESTER (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY 63000CT PC+POLYESTER (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A permanent antistatic PC-Alloy compound that features transparency and superior cleanliness for advanced semiconductor packaging applications
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.700 % | 0.700 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | SABIC Method |
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 260 °C |
16 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 5 mm/min; ISO 527 |
| 35.0 MPa | 5080 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 140 % | 140 % | 5 mm/min; ISO 527 |
| 200 % | 200 % | Type I, 10 mm/min; SABIC - Japan Method | |
| Tensile Modulus | 1.16 GPa | 168 ksi | 50 mm/min; ASTM D638 |
| 1.18 GPa | 171 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 50.0 MPa | 7250 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.14 GPa | 165 ksi | 2 mm/min; ISO 178 |
| 1.16 GPa | 168 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 5.80 J/cm | 10.9 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 6.90 J/cm² | 32.8 ft-lb/in² | ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 83.0 °C @Thickness 6.40 mm |
181 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 73.0 °C @Thickness 6.40 mm |
163 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 10 % @Thickness 2.54 mm |
10 % @Thickness 0.100 in |
ASTM D1003 |
| Transmission, Visible | 81 % | 81 % | 2.54 mm; ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 12 ohm-cm | 12 ohm-cm | ASTM D257 |
| Surface Resistance | 12 ohm | 12 ohm | ASTM D257 |
| Static Decay | 2.0 sec | 2.0 sec | 5000V to <50V; FTMS101B |
Users viewing this material also viewed the following:
- Lucite International Colacryl ® TS2050 Acrylic Resin
- Styron DL 220NA Carboxylated SB
- Zeon Chemicals Nipol® 1031 Nitrile Elastomer
- A. Schulman POLYFLAM™ RPP 1174 Talc Filled, Homopolymer Polypropylene
- Eastman Tritan TX1500HF Copolyester
- Cotronics Duralco™ 4461 Electrically Resistant, Low Viscosity Epoxy Adhesive, Coating, and Sealant
- Epoxy Technology EPO-TEK® 431 Copper Filled Epoxy
- Chosun Refractories A-3 Insulating Firebrick
- 3M Scotchcal™ 8000-12 Graphic Film
- Aaron Industries AAROPRENE® GFN 6013 Glass Filled Nylon 6
Copyright © lookpolymers.com All Rights Reserved