Total PPH 11012 Polypropylene Homopolymer, Injection Molding

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded
Manufacturer Total Atofina
Trade Name PPH
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total PPH 11012 Polypropylene Homopolymer, Injection Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polypropylene PPH 11012 is a nucleated controlled-rheology antistatic homopolymer with a high melt flow index of 55 g/10 min.Polypropylene PPH 11012 is characterized by high fluidity for high speed injection of thin wall articles such as dairy pots & tubs, salad trays, caps & closures and video cassette boxes.Polypropylene PPH 11012 has a highly antistatic nature that allows for shorter cycle times and easy demolding.Information provided by Total Petrochemicals.
Physical Properties Metric English Comments
Specific Gravity 0.905 g/cc
0.905 g/cc
ISO 1183
Bulk Density 0.525 g/cc
0.0190 lb/in³
ISO 1183
Melt Flow 55 g/10 min

@Load 2.16 kg,
Temperature 230 °C
55 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 100
100
ISO 2039-2
Tensile Strength, Yield 34.0 MPa
4930 psi
ISO 527-2
Elongation at Yield 9.0 %
9.0 %
ISO 527-2
Tensile Modulus 1.70 GPa
247 ksi
ISO 527-2
Flexural Modulus 1.60 GPa
232 ksi
ISO 178
Izod Impact, Notched (ISO) 2.50 kJ/m²
1.19 ft-lb/in²
ISO 180
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Melting Point 165 °C
329 °F
ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 105 °C
221 °F
120°C per hour; ISO 752
Deflection Temperature at 1.8 MPa (264 psi) 58.0 °C
136 °F
120°C per hour; ISO 752
Vicat Softening Point 87.0 °C

@Load 5.10 kg
189 °F

@Load 11.2 lb
50°C per hour; ISO 306
152 °C

@Load 1.02 kg
306 °F

@Load 2.25 lb
50°C per hour; ISO 306