Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 21.0 MPa | 3050 psi | |
Plastcom SLOVALEN EH 96 FRD 2 PP, flame retardant FeaturesDetermined for environment, where contact with water is possible, because the electric properties do not change by conditioning. Application - terminals, coil forms, guides in washing machin.. |
|||
Flexural Strength | 21.0 MPa | 3050 psi | |
Plastcom SLOVALEN PC 71 T 15 PP, 15% mineral filling FeaturesModified PP for injection moulding with the content of 15% mineral filling. Increased rigidity, strength and thermal. Decreased shrinkage. General application in all industry branches - pack.. |
|||
Flexural Strength | 21.0 MPa | 3050 psi | |
Plastcom SLOVALEN PQ 81 T 30 PP, 30% mineral filling FeaturesModified PP for injection moulding with the content of 30% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shrinkage. Gene.. |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ASTM D790 |
SABIC M40053S High Density Polyethylene for Injection Molding Product Description: M40053S is a UV stabilized high density polyethylene grade with a narrow molecular weight distribution suitable for injection molding applications. It has been designed to pro.. |
|||
Flexural Strength | 21.0 MPa | 3050 psi | |
Plastcom SLOVALEN PC 93 T 5 PP reinforced with 5% mineral filler Features: Modified PP for injection moulding with the content of 5% mineral filling. Increased rigidity, strength and thermal. Decreased shrinkage. General application in all industry branches.Packa.. |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP TH0450C PU LNP* Thermocomp* TH0450C is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP TH0450C PUR (Asia Pacific) LNP* Thermocomp* TH0450C is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP TH0815A LNP* THERMOCOMP* TH0815A is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP TH0815A PUR (Asia Pacific) LNP* THERMOCOMP* TH0815A is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
Flexural Strength | 21.0 MPa | 3050 psi | Olsen; ASTM D747 |
UBE B128 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ISO 178 |
Borealis Daplen™ EF005AE Polypropylene TPO Compound Daplen™ EF005AE is a 10% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness, give.. |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ISO 178 |
Borealis Daplen™ EH104AE Polypropylene TPO Compound Daplen™ EH104AE is a 10% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness, high.. |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ISO 178 |
Borealis EE002AE Polypropylene Elastomer Modified EE002AE is a reactor elastomer modified polypropylene compound intended for injection molding. The product is available in natural color. This material has excellent balanced mechanical properties.. |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ASTM D790 |
UBE UBESTA® 3030JI5L Plasticized Automotive Grade Nylon 12 Description: UBE UBESTA® Automotive grade Nylon 12Comments: meet SAE J844, DIN73378 HIPHLInformation provided by UBE. |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ASTM D790 |
UBE UBESTA® 3030JI6L Plasticized Automotive Grade Nylon 12 Description: UBE UBESTA® Automotive grade Nylon 12Comments: for multilayer tubeInformation provided by UBE. |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ASTM D790 |
Aclo Accucomp Polyethylene HD0200L High Density |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ASTM D790 |
Aclo Accucomp Polyethylene HD0202L High Density |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ASTM D790 |
Aclo Accucomp Polypropylene CPO407L Copolymer |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ASTM D790 |
Aclo Accutech Polypropylene Copolymer CP0437M10CL Mica Reinforced Coupled |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ASTM D790 |
Aclo Accutech Polypropylene Copolymer CP0437M10L Mica Reinforced |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ASTM D790 |
Aclo Accutech Polypropylene Copolymer CP0437M20L Mica Reinforced |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ASTM D790 |
Aclo Accutech Polypropylene Copolymer CP0437M30L Mica Reinforced |
|||
Flexural Strength | 21.0 MPa @Temperature 120 °C |
3050 psi @Temperature 248 °F |
ASTM Test |
BASF Ultramid® 8202C HS PA6 (Dry) Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also.. |
|||
Flexural Strength | 21.0 MPa @Temperature 120 °C |
3050 psi @Temperature 248 °F |
ASTM Test |
BASF Ultramid® 8202C PA6 (Dry) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique .. |
|||
Flexural Strength | 21.0 MPa @Temperature 120 °C |
3050 psi @Temperature 248 °F |
ASTM Test |
BASF Ultramid® 8202CQ PA6 (Dry) Ultramid 8202CQ is a low viscosity, PA6 injection molding homopolymer, possessing a modified crystalline structure or increased property performance and faster cycles. It is also available in pigme.. |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ASTM D790 |
Aclo Accutech Polyethylene HD0204UVL High Density UV Stabilized |
|||
Flexural Strength | 21.0 MPa | 3050 psi | |
Plastcom SLOVALEN PQ 83 T 40 PP, 40% mineral filling FeaturesModified PP for injection moulding with the content of 40% mineral filling, uv stabilized. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased .. |
|||
Flexural Strength | 21.0 MPa | 3050 psi | ISO 178 |
Unitika EX-1030 PA6, Conditioned High-impact nylonInformation provided by Unitika Ltd. |